PA6 Ultramid® 8202CHS BASF GERMANY

210

Unit Price:US$ 2,824 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
70MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜high strength｜Oil resistant
Application Areas:Helmet｜Automotive Applications｜Engine parts
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179	3.5 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
Impact strength of cantilever beam gap	-40°C	ASTM D256	32 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	48 J/m
Dart impact	23°C	Internal Method	122 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.71mm	UL 94	V-2
	UL flame retardant rating	3.0mm	UL 94	V-2
		UL flame retardant rating	6.0mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield,-40°C	ASTM D638	137 Mpa
	tensile strength	Yield,23°C	ASTM D638	90.0 Mpa
	tensile strength	tensile strength	Yield,80°C	ASTM D638	40.0 Mpa
Tensile modulus	150°C	ISO 527-2	445 Mpa
	Tensile modulus	120°C	ISO 527-2	550 Mpa
	Tensile modulus	Tensile modulus	80°C	ISO 527-2	750 Mpa
bending strength	23°C	ISO 178	95.0 Mpa
	bending strength	121°C	ASTM D790	21.0 Mpa
		bending strength	65°C	ASTM D790	30.0 Mpa
			bending strength	23°C	ASTM D790	110 Mpa
			bending strength	bending strength	-40°C	ASTM D790	183 Mpa
Bending modulus	23°C	ISO 178	2800 Mpa
	Bending modulus	121°C	ASTM D790	385 Mpa
		Bending modulus	90°C	ASTM D790	440 Mpa
			Bending modulus	65°C	ASTM D790	600 Mpa
			Bending modulus	Bending modulus	23°C	ASTM D790	3170 Mpa
tensile strength	Yield,121°C	ASTM D638	30.0 Mpa
	tensile strength	Yield,-40°C	ISO 527-2	137 Mpa
		tensile strength	Yield,23°C	ISO 527-2	88.0 Mpa
		tensile strength	tensile strength	Yield,80°C	ISO 527-2	40.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	4.0 %
elongation	Break,-40°C	ASTM D638	5.0 %
	elongation	Break,23°C	ASTM D638	12 %
		elongation	Break,80°C	ASTM D638	>100 %
		elongation	elongation	Break,121°C	ASTM D638	>100 %
Nominal tensile fracture strain	-40°C	ISO 527-2	5.0 %
Bending modulus	-40°C	ASTM D790	3370 Mpa
Nominal tensile fracture strain	23°C	ISO 527-2	7.0 %
	Nominal tensile fracture strain	80°C	ISO 527-2	>100 %
	Nominal tensile fracture strain	Nominal tensile fracture strain	120°C	ISO 527-2	>100 %
Tensile modulus	-40°C	ISO 527-2	4090 Mpa
Tensile modulus	Tensile modulus	23°C	ISO 527-2	3700 Mpa
tensile strength	Yield,120°C	ISO 527-2	30.0 Mpa
	tensile strength	Yield,150°C	ISO 527-2	25.0 Mpa
		tensile strength	Break,-40°C	ASTM D638	130 Mpa
			tensile strength	Break,23°C	ASTM D638	90.0 Mpa
				tensile strength	Break,80°C	ASTM D638	35.0 Mpa
				tensile strength	tensile strength	Break,121°C	ASTM D638	25.0 Mpa
elongation	Yield,-40°C	ASTM D638	3.0 %
	elongation	Yield,23°C	ASTM D638	4.0 %
		elongation	Yield,80°C	ASTM D638	25 %
		elongation	elongation	Yield,121°C	ASTM D638	27 %

thermal performance	Test Condition	Test Method	Test Result
RTI Str	6.0mm	UL 746	105 °C
	RTI Str	3.0mm	UL 746	105 °C
		RTI Str	1.5mm	UL 746	105 °C
		RTI Str	RTI Str	0.71mm	UL 746	95.0 °C
RTI Imp	6.0mm	UL 746	105 °C
RTI Elec	1.5mm	UL 746	130 °C
	RTI Elec	3.0mm	UL 746	130 °C
	RTI Elec	RTI Elec	6.0mm	UL 746	130 °C
RTI Imp	0.71mm	UL 746	95.0 °C
	RTI Imp	1.5mm	UL 746	105 °C
	RTI Imp	RTI Imp	3.0mm	UL 746	105 °C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	190 °C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	165 °C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	75.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	65.0 °C
Melting temperature		ASTM D3418	220 °C
Melting temperature	Melting temperature		ISO 3146	220 °C
Linear coefficient of thermal expansion	MD	ASTME831	8.1E-05 cm/cm/°C
RTI Elec	0.71mm	UL 746	130 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.13 g/cm³
density	density		ISO 1183	1.13 g/cm³
Shrinkage rate	MD：3.18mm		0.90 %
Water absorption rate	24hr	ASTM D570	1.6 %
	Water absorption rate	23°C,24hr	ISO 62	1.6 %
		Water absorption rate	Saturation	ASTM D570	9.3 %
			Water absorption rate	Saturation,23°C	ISO 62	9.3 %
				Water absorption rate	Equilibrium,50%RH	ASTM D570	2.6 %
				Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.6 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	V
Dielectric strength	1.50mm	ASTM D149	30 KV/mm
Volume resistivity		IEC 60093	>1.0E+13 ohms·cm
Volume resistivity	Volume resistivity	1.50mm	ASTM D257	>1.0E+13 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Ultramid® 8202CHS BASF GERMANY

Material Description

Technical Data Sheet Compare

Technical Data Sheet