Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 8202CHS BASF GERMANY
Ultramid®
Helmet、Automotive Applications、Engine parts
Thermal stability、high strength、Oil resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/8202CHS |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 3.5 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 32 J/m |
| 23°C | ASTM D256 | 48 J/m | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Dart impact | 23°C | 内部方法 | 122 J |
| hardness | Test Condition | Test Method | BASF GERMANY/8202CHS |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/8202CHS |
|---|---|---|---|
| elongation | Break,121°C | ASTM D638 | >100 % |
| Tensile modulus | 80°C | ISO 527-2 | 750 Mpa |
| Flexural modulus | -40°C | ASTM D790 | 3370 Mpa |
| bending strength | 23°C | ASTM D790 | 110 Mpa |
| 65°C | ASTM D790 | 30.0 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 3700 Mpa |
| tensile strength | 断裂,80°C | ASTM D638 | 35.0 Mpa |
| 屈服,23°C | ASTM D638 | 90.0 Mpa | |
| elongation | Yield,121°C | ASTM D638 | 27 % |
| Tensile modulus | 150°C | ISO 527-2 | 445 Mpa |
| tensile strength | 屈服,150°C | ISO 527-2 | 25.0 Mpa |
| Flexural modulus | 90°C | ASTM D790 | 440 Mpa |
| bending strength | 121°C | ASTM D790 | 21.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2800 Mpa |
| Nominal tensile fracture strain | -40°C | ISO 527-2 | 5.0 % |
| 120°C | ISO 527-2 | >100 % | |
| bending strength | -40°C | ASTM D790 | 183 Mpa |
| tensile strength | 屈服,-40°C | ASTM D638 | 137 Mpa |
| Break,121°C | ASTM D638 | 25.0 Mpa | |
| 屈服,-40°C | ISO 527-2 | 137 Mpa | |
| Tensile modulus | -40°C | ISO 527-2 | 4090 Mpa |
| tensile strength | 断裂,23°C | ASTM D638 | 90.0 Mpa |
| elongation | 屈服,-40°C | ASTM D638 | 3.0 % |
| Tensile modulus | 120°C | ISO 527-2 | 550 Mpa |
| Nominal tensile fracture strain | 80°C | ISO 527-2 | >100 % |
| elongation | 屈服,80°C | ASTM D638 | 25 % |
| Flexural modulus | 121°C | ASTM D790 | 385 Mpa |
| bending strength | 23°C | ISO 178 | 95.0 Mpa |
| tensile strength | 屈服,120°C | ISO 527-2 | 30.0 Mpa |
| 屈服,80°C | ASTM D638 | 40.0 Mpa | |
| 屈服,23°C | ISO 527-2 | 88.0 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.0 % |
| elongation | 断裂,-40°C | ASTM D638 | 5.0 % |
| Flexural modulus | 65°C | ASTM D790 | 600 Mpa |
| elongation | 断裂,80°C | ASTM D638 | >100 % |
| 屈服,23°C | ASTM D638 | 4.0 % | |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 7.0 % |
| Flexural modulus | 23°C | ASTM D790 | 3170 Mpa |
| tensile strength | Yield,121°C | ASTM D638 | 30.0 Mpa |
| 屈服,80°C | ISO 527-2 | 40.0 Mpa | |
| elongation | 断裂,23°C | ASTM D638 | 12 % |
| tensile strength | 断裂,-40°C | ASTM D638 | 130 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/8202CHS |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| 1.50mm | ASTM D257 | >1.0E+13 ohms·cm | |
| dielectric strength | 1.50mm | ASTM D149 | 30 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | BASF GERMANY/8202CHS |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-2 |
| 6.0mm | UL 94 | V-2 | |
| 1.5mm | UL 94 | V-2 | |
| 0.71mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | BASF GERMANY/8202CHS |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.90 % | |
| Water absorption rate | 饱和 | ASTM D570 | 9.3 % |
| 24hr | ASTM D570 | 1.6 % | |
| 23°C,24hr | ISO 62 | 1.6 % | |
| 平衡,50%RH | ASTM D570 | 2.6 % | |
| 平衡,23°C,50%RH | ISO 62 | 2.6 % | |
| 饱和,23°C | ISO 62 | 9.3 % | |
| density | ASTM D792 | 1.13 g/cm³ | |
| ISO 1183 | 1.13 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/8202CHS |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 75.0 °C |
| RTI Elec | 6.0mm | UL 746 | 130 °C |
| RTI Imp | 1.5mm | UL 746 | 105 °C |
| RTI Str | 6.0mm | UL 746 | 105 °C |
| melting temperature | ASTM D3418 | 220 °C | |
| RTI Elec | 0.71mm | UL 746 | 130 °C |
| 3.0mm | UL 746 | 130 °C | |
| RTI Imp | 3.0mm | UL 746 | 105 °C |
| melting temperature | ISO 3146 | 220 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 190 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 165 °C | |
| RTI Str | 1.5mm | UL 746 | 105 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 65.0 °C |
| RTI Str | 3.0mm | UL 746 | 105 °C |
| RTI Elec | 1.5mm | UL 746 | 130 °C |
| Linear coefficient of thermal expansion | MD | ASTME831 | 8.1E-05 cm/cm/°C |
| RTI Imp | 6.0mm | UL 746 | 105 °C |
| RTI Str | 0.71mm | UL 746 | 95.0 °C |
| RTI Imp | 0.71mm | UL 746 | 95.0 °C |