plas
Log In | Sign Up
CategoriesAll
Plastic Raw Materials
Modified Plastics
Plastic Additives
Color Masterbatch
Plastic Datasheets
Plastic News
About Us
Home
Plastic Raw Materials
PA6

PA6 Amilan®  CM1056 TORAY JAPAN

215
  • Unit Price:US$ 2,734 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    43MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:Blow molding grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-40°CkJ/m²16 54
Impact strength of simply supported beam without notch23°C无断裂 --
Basic PerformanceTest ConditionTest MethodTest Result
Water absorption rate23℃ASTM D-570Dry｜8.0 %
Water absorption rate23℃ASTM D-5703.0%Water｜- %
Water absorption rate23℃，24hrASTM D-570Dry｜1.7 %
Water absorption rate23℃，24hrASTM D-5703.0%Water｜- %
mechanical propertiesTest ConditionTest MethodTest Result
Bending modulus-40℃ASTM D-7903.0%Water｜- GPa
Bending modulus23℃ASTM D-790Dry｜2.1 GPa
Bending modulus23℃ASTM D-7903.0%Water｜0.7 GPa
Bending modulus80℃ASTM D-790Dry｜0.5 GPa
Bending modulus80℃ASTM D-7903.0%Water｜- GPa
Suspended wall beam without notch impact strength23℃ASTM D-256Dry｜不断裂 kJ/m²
Suspended wall beam without notch impact strength23℃ASTM D-2563.0%Water｜- kJ/m²
Elongation at Break-40℃ASTM D-638Dry｜15 %
Elongation at Break-40℃ASTM D-6383.0%Water｜5.0 %
tensile strengthYield,80℃ASTM D-638Dry｜25 Mpa
Rockwell hardness23℃ASTM D-7853.0%Water｜- R scale
Impact strength of cantilever beam gap23℃ASTM D-256Dry｜205 J/m
Impact strength of cantilever beam gap23℃ASTM D-2563.0%Water｜690 J/m
Impact strength of cantilever beam gap-40℃ASTM D-256Dry｜175 J/m
Impact strength of cantilever beam gap-40℃ASTM D-2563.0%Water｜- J/m
Elongation at Break23℃ASTM D-638Dry｜<200 %
Elongation at Break23℃ASTM D-6383.0%Water｜<200 %
Elongation at Break80℃ASTM D-638Dry｜<200 %
Elongation at Break80℃ASTM D-6383.0%Water｜<200 %
Bending modulus-40℃ASTM D-790Dry｜2.9 GPa
tensile strengthYield,80℃ASTM D-6383.0%Water｜20 Mpa
tensile strengthYield,23℃ASTM D-638Dry｜60 Mpa
tensile strengthYield,23℃ASTM D-6383.0%Water｜35 Mpa
bending strength-40℃ASTM D-790Dry｜130 Mpa
bending strength-40℃ASTM D-7903.0%Water｜- Mpa
tensile strength80°CMPa25.0 20.0
Tensile strainBreak,-40°C%3.5 1.0
Tensile strainBreak,23°C%50
Tensile strainBreak,80°C%50
Bending modulus-40°CMPa2900 --
Bending modulus23°CMPa2100 700
Bending modulus80°CMPa500 --
bending strength-40°CMPa130 --
bending strength23°CMPa80.0 --
Taber abraser1000Cyclesmg6.00to7.00 --
tensile strength-40°CMPa105 95.0
tensile strength23°CMPa60.0 35.0
bending strength23℃ASTM D-790Dry｜80 Mpa
bending strength23℃ASTM D-7903.0%Water｜- Mpa
tensile strengthYield,-40℃ASTM D-638Dry｜105 Mpa
tensile strengthYield,-40℃ASTM D-6383.0%Water｜95 Mpa
Rockwell hardness23℃ASTM D-785Dry｜114 R scale
Rockwell hardnessASTM D785114
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,Unannealed°C160 --
Hot deformation temperature1.8MPa,Unannealed°C51.0 --
Melting temperature°C225 --
Linear coefficient of thermal expansionMDcm/cm/°C8.0E-5到9.0E-5 --
Melting temperatureDSC225 °C
Hot deformation temperature1.86MPaASTM D-648Dry｜67 °C
Hot deformation temperature1.86MPaASTM D-6483.0%Water｜- °C
Hot deformation temperature0.46MPaASTM D-648Dry｜160 °C
Hot deformation temperature0.46MPaASTM D-6483.0%Water｜- °C
Linear coefficient of thermal expansionASTM D-696Dry｜8-9 10-5/℃
Linear coefficient of thermal expansionASTM D-6963.0%Water｜- 10-5/℃
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rate23°C,24hr%1.7 --
Water absorption rateSaturation,23°C%8.0 --
densityASTM D792/ISO 11831.09
Water absorption rateASTM D570/ISO 621.7 %
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-Sale,23°C114 --
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.