PA6 CM1056 TORAY JAPAN
Amilan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/CM1056 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | kJ/m² | 16 54 |
| 23°C | 无断裂 -- |
| hardness | Test Condition | Test Method | TORAY JAPAN/CM1056 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | 114 -- |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/CM1056 |
|---|---|---|---|
| Water absorption rate | 23℃ | ASTM D-570 | 3.0%Water｜- % |
| 23℃，24hr | ASTM D-570 | 3.0%Water｜- % |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM1056 |
|---|---|---|---|
| Flexural modulus | -40°C | MPa | 2900 -- |
| elongation at break | -40℃ | ASTM D-638 | 3.0%Water｜5.0 % |
| Impact strength of cantilever beam gap | -40℃ | ASTM D-256 | 3.0%Water｜- J/m |
| Taber abraser | 1000Cycles | mg | 6.00to7.00 -- |
| tensile strength | 23°C | MPa | 60.0 35.0 |
| Flexural modulus | -40℃ | ASTM D-790 | Dry｜2.9 GPa |
| 23℃ | ASTM D-790 | 3.0%Water｜0.7 GPa | |
| bending strength | 23°C | MPa | 80.0 -- |
| Rockwell hardness | ASTM D785 | 114 | |
| tensile strength | 80°C | MPa | 25.0 20.0 |
| Tensile strain | 断裂,23°C | % | 50 |
| Rockwell hardness | 23℃ | ASTM D-785 | Dry｜114 R scale |
| Tensile strain | 断裂,-40°C | % | 3.5 1.0 |
| bending strength | 23℃ | ASTM D-790 | 3.0%Water｜- Mpa |
| Suspended wall beam without notch impact strength | 23℃ | ASTM D-256 | 3.0%Water｜- kJ/m² |
| elongation at break | 80℃ | ASTM D-638 | 3.0%Water｜<200 % |
| tensile strength | 屈服,23℃ | ASTM D-638 | 3.0%Water｜35 Mpa |
| Tensile strain | 断裂,80°C | % | 50 |
| tensile strength | -40°C | MPa | 105 95.0 |
| Flexural modulus | 23°C | MPa | 2100 700 |
| 80℃ | ASTM D-790 | 3.0%Water｜- GPa | |
| tensile strength | 屈服,-40℃ | ASTM D-638 | 3.0%Water｜95 Mpa |
| bending strength | -40℃ | ASTM D-790 | 3.0%Water｜- Mpa |
| elongation at break | 23℃ | ASTM D-638 | 3.0%Water｜<200 % |
| tensile strength | 屈服,80℃ | ASTM D-638 | 3.0%Water｜20 Mpa |
| Flexural modulus | 80°C | MPa | 500 -- |
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 3.0%Water｜690 J/m |
| bending strength | -40°C | MPa | 130 -- |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/CM1056 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.09 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.7 % |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM1056 |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | % | 8.0 -- |
| 23°C,24hr | % | 1.7 -- |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM1056 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 160 -- |
| melting temperature | °C | 225 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 8.0E-5到9.0E-5 -- |
| Heat distortion temperature | 0.46MPa，HDT | ASTM D-648 | 3.0%Water｜- °C |
| 1.86MPa，HDT | ASTM D-648 | 3.0%Water｜- °C | |
| 1.8MPa,未退火，HDT | °C | 51.0 -- | |
| Linear coefficient of thermal expansion | ASTM D-696 | 3.0%Water｜- 10-5/℃ | |
| melting temperature | DSC | 225 °C |