PA612 Zytel® 77G43L NC010 DUPONT USA

463

Unit Price:US$ 7,620 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜high strength
Application Areas:Automotive components｜Electronic and Electrical Applications
Color:--
Grade:Injection grade

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Top out temperature			210	°C
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	85	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
Burning rate	1.00 mm	ISO 3795	21	mm/min
UL flame retardant rating		UL 94	HB
FMVSS combustion rate		FMVSS 302	B
雾化 - G-value (condensate)		ISO 6452	1.0E-4	g
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	12500	Mpa
Bending modulus		ISO 178	11000	Mpa
Tensile strain	Break	ISO 527-2	3.0	%
tensile strength	Break	ISO 527-2	200	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
Drying time - hot air dryer			2.0 to 4.0	hr
Suggested maximum moisture content			0.20	%
Processing (melt) temperature			280 to 300	°C
Melt Temperature, Optimum			290	°C
Mold temperature			70 to 120	°C
Maintain pressure			50.0 to 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Maximum Screw Tangential Speed			12	m/min
Mold Temperature, Optimum			100	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow : 55 to 160°C	ISO 11359-2	1.4E-4	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 23°C	ISO 11359-2	7.5E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.1E-4	cm/cm/°C
			Linear coefficient of thermal expansion	Flow : 55 to 160°C	ISO 11359-2	1.3E-5	cm/cm/°C
				Linear coefficient of thermal expansion	Flow : -40 to 23°C	ISO 11359-2	2.1E-5	cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.4E-5	cm/cm/°C
Melting temperature		ISO 11357-3	218	°C
Glass transition temperature		ISO 11357-2	65.0	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	203	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	217	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Stickiness		ISO 307	145	cm³/g
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	0.70	%
Water absorption rate	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	1.7	%
Shrinkage rate	Flow	ISO 294-4	0.30	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.80	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 62631-3-1	1.0E+13	ohms·m
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R -Sale	ISO 2039-2	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Guangyan	US$ 8420 /MT

Supplier Join

Get App

Top

PA612 Zytel® 77G43L NC010 DUPONT USA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index