PC INFINO® HP-1000XA K24970 LOTTE KOREA
191
- Unit Price:US$ 3,568 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility
- Application Areas:Automotive Applications｜Application in the automotive field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 113 |
| R级 | ISO 2039-2 | 113 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Annealed,4.00mm | ISO 75-2/B | 125 °C |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 110 °C | |
| 1.8MPa,Unannealed,4.00mm | ISO 75-2/A | 102 °C | |
| 1.8MPa,Annealed,4.00mm | ISO 75-2/A | 112 °C | |
| vicat | -- | ISO 306/B50 | 123 °C |
| -- | ISO 306/B120 | 125 °C | |
| Heat Deflection Temperature | 0.45MPa,Unannealed,4.00mm | ISO 75-2/B | 123 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 49 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 45 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD:3.20mm | ISO 2577 | 0.40-0.70 % |
| melt mass-flow rate | 250°C/10.0kg | ASTM D1238 | 27 g/10min |
| 250°C/10.0kg | ISO 1133 | 27 g/10min | |
| shrinkage rate | MD：3.20mm | ASTM D955 | 0.40-0.70 % |
| TD：3.20mm | ASTM D955 | 0.40-0.70 % | |
| TD:3.20mm | ISO 2577 | 0.40-0.70 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2000 Mpa | |
| ISO 527-2/50 | 2000 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 54.0 Mpa |
| 屈服 | ISO 527-2/50 | 50.0 Mpa | |
| 断裂 | ASTM D638 | 59.0 Mpa | |
| 断裂 | ISO 527-2/50 | 53.0 Mpa | |
| elongation | 断裂 | ASTM D638 | 100 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| flexural modulus | ASTM D790 | 2000 Mpa | |
| ISO 178 | 2100 Mpa | ||
| bending strength | ASTM D790 | 74.0 Mpa | |
| ISO 178 | 80.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.