'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPS FORTRON® 1140L4 SF3001 CELANESE USA
489
- Unit Price:US$ 8,040 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:173MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High temperature resistance｜enhance｜Glass fiber reinforced｜Injection grade｜Medium melt viscosity
- Application Areas:Fiber grade｜During injection molding｜Slight flash
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
| Filling analysis | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| SpecificHeatCapacity of Melt | Internal Method | 1500 | J/kg/°C | |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 53 | kJ/m² |
| -30°C | ISO 179/1eU | 53 | kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 | kJ/m² |
| -30°C | ISO 179/1eA | 10 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 | kJ/m² |
| 23°C | ISO 180/1A | 10 | kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 34 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.38mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 | ||
| 3.0mm | UL 94 | 5VA | ||
| Extreme Oxygen Index | ISO 4589-2 | 47 | % | |
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | ASTM-D570 | 0.02 | % | |
| density | ISO 1183 | 1.65 | g/cm³ | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| bending strength | ISO 178 | 285 | Mpa | |
| Bending modulus | 23°C | ISO 178 | 14500 | Mpa |
| elongation | Break | ISO 527-2/1A/5 | 1.9 | % |
| Break,23°C | ASTM D638 | 1.7 | % | |
| tensile strength | Break | ISO 527-2/1A/5 | 195 | Mpa |
| Break,23°C | ASTM D638 | 200 | Mpa | |
| Rockwell hardness | ASTM-D785 | 100 | R-Scale | |
| Impact strength of cantilever beam gap | ISO 180/1A | 10 | kJ/m² | |
| Bending modulus | ISO 178 | 14500 | Mpa | |
| bending strength | ISO 178 | 285 | Mpa | |
| Tensile modulus | ISO 527 | 14700 | Mpa | |
| tensile strength | ISO 527 | 195 | Mpa | |
| Tensile modulus | -40°C | ASTM D638 | 14500 | Mpa |
| 75°C | ASTM D638 | 11900 | Mpa | |
| 150°C | ASTM D638 | 4270 | Mpa | |
| 200°C | ASTM D638 | 3240 | Mpa | |
| -- | ISO 527-2/1A/1 | 14700 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 4.2E-05 | cm/cm/°C |
| UL flame retardant rating | UL 94 | V-0 | ||
| Hot deformation temperature | 1.80Mpa | ISO 75-A | 270 | °C |
| Glass transition temperature | ISO 11357-2 | 90.0 | °C | |
| Melting temperature | ISO 11357-3 | 280 | °C | |
| Hot deformation temperature | 0.45MPa,Annealed | ASTM D648 | 280 | °C |
| 1.8MPa,Unannealed | ASTM D648 | 265 | °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 270 | °C | |
| 8.0MPa,Unannealed | ISO 75-2/C | 215 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.6E-05 | cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | ISO 294-4 | 0.2-0.6 | % | |
| TD | ISO 294-4 | 0.40-0.60 | % | |
| MD | ISO 294-4 | 0.20-0.60 | % | |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.020 | % |
| Shrinkage rate | MD | ASTM D955 | 0.20-0.30 | % |
| TD | ASTM D955 | 0.50-0.70 | % | |
| density | ASTMD792 | 1.65 | g/cm³ | |
| Specific volume | ASTM D792 | 0.611 | cm³/g | |
| Biochemical properties | Test Condition | Test Method | Test Result | Test Unit |
| Filling amount | 40 | % | ||
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | -- | ASTM D257 | 1E+16 | ohms·cm |
| -- | IEC 60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 28 | KV/mm | |
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Dielectric constant | 1kHz | ASTM D150 | 3.50 | |
| 1MHz | ASTM D150 | 3.50 | ||
| 1MHz | IEC 60250 | 4.60 | ||
| Dissipation factor | 1kHz | ASTM D150 | 1E-03 | |
| 1MHz | ASTM D150 | 1E-03 | ||
| 1MHz | IEC 60250 | 6.2E-03 | ||
| Arc resistance | ASTM D495 | 134 | sec | |
| Compared to the anti leakage trace index | IEC 60112 | PLC 4 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Scale | ASTM D785 | 100 | |
| M-Sale | ISO 2039-2 | 100 | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | Internal Method | 3.18 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.