PA66

PA66 Ultramid® A3EG6 BASF USA

284

Unit Price:US$ 3,671 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
39MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜Oil resistant｜dimensional stability
Application Areas:machine｜Mechanical components｜Shell｜Electrical components｜Electronic insulation
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	85 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	70 kJ/m²

flammability	Test Condition	Test Method	Test Result
Flammability level		UL 94	HB
Polymer Abbreviation			PA66-GF30

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	280 Mpa
Bending modulus		ISO 178	8600 Mpa
Tensile creep modulus	1000 hr	ISO 899-1	-- Mpa
Tensile strain	Break	ISO 527-2	3.0 %
tensile strength	Break	ISO 527-2	190 Mpa
Tensile modulus		ISO 527-2	10000 Mpa

injection	Test Condition	Test Method	Test Result
Processing (melt) temperature			280 to 300 °C
Mold temperature			80 to 90 °C

thermal performance	Test Condition	Test Method	Test Result
Maximum operating temperature	短周期操作		240 °C
Temperature index - at 50% loss of tensile strength	--6	IEC 60216	135 °C
Temperature index - at 50% loss of tensile strength	Temperature index - at 50% loss of tensile strength	--5	IEC 60216	165 °C
thermal conductivity		DIN 52612	0.35 W/m/K
specific heat			1500 J/kg/°C
Melting temperature		ISO 11357-3	260 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	250 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	250 °C

Physical properties	Test Condition	Test Method	Test Result
Mold Shrinkage - Constrained			0.55 %
Stickiness	96% H2SO4	ISO 307	145 cm³/g
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.5 to 1.9 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	5.2 to 5.8 %
Melt Volume Flow Rate (MVR)	275°C/5.0 kg	ISO 1133	40.0 cm3/10min
Apparent density			0.70 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	1 MHz	IEC 60250	3.50
Dissipation factor	1 MHz	IEC 60250	0.014
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Surface resistivity		IEC 60093	-- ohms
Compared to the anti leakage trace index	Solution A	IEC 60112	V

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.