PA66 A3EG6 BASF USA
Ultramid®
machine、Mechanical components、Shell、Electrical components、Electronic insulation
High rigidity、Oil resistant、dimensional stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF USA/A3EG6 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 85 kJ/m² |
| -30°C | ISO 179/1eU | 70 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF USA/A3EG6 |
|---|---|---|---|
| Tensile creep modulus | 1000 hr | ISO 899-1 | -- Mpa |
| Tensile modulus | ISO 527-2 | 10000 Mpa | |
| bending strength | ISO 178 | 280 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Flexural modulus | ISO 178 | 8600 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 190 Mpa |
| Electrical performance | Test Condition | Test Method | BASF USA/A3EG6 |
|---|---|---|---|
| Dissipation Factor | 1 MHz | IEC 60250 | 0.014 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | V |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| relative permittivity | 1 MHz | IEC 60250 | 3.50 |
| Surface Resistivity | IEC 60093 | -- ohms |
| flammability | Test Condition | Test Method | BASF USA/A3EG6 |
|---|---|---|---|
| Flammability level | UL 94 | HB | |
| Polymer Abbreviation | PA66-GF30 |
| physical property | Test Condition | Test Method | BASF USA/A3EG6 |
|---|---|---|---|
| Apparent density | 0.70 g/cm³ | ||
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.5 to 1.9 % |
| Mold Shrinkage - Constrained | 0.55 % | ||
| viscosity number | 96% H2SO4 | ISO 307 | 145 cm³/g |
| Melt volume flow rate | 275°C/5.0 kg | ISO 1133 | 40.0 cm3/10min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 5.2 to 5.8 % |
| Thermal performance | Test Condition | Test Method | BASF USA/A3EG6 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 260 °C | |
| thermal conductivity | DIN 52612 | 0.35 W/m/K | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 250 °C |
| Temperature index - at 50% loss of tensile strength | --5 | IEC 60216 | 165 °C |
| --6 | IEC 60216 | 135 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 250 °C |
| specific heat | 1500 J/kg/°C | ||
| maximum service temperature | 短周期操作 | 240 °C |
| injection | Test Condition | Test Method | BASF USA/A3EG6 |
|---|---|---|---|
| Processing (melt) temperature | 280 to 300 °C | ||
| Temperature | 80 to 90 °C |