PA66 AKROMID® A3GF50 AKRO-PLASTIC GERMANY

844

Unit Price:US$ 3,090 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
60MT
Delivery Terms:
FOB
Port of Loading :
Shenzhen Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:high strength｜heat-resisting｜dimensional stability ｜Electrical performance｜Processability｜Filler: Glass fiber reinforced material｜50%｜Filler by weight
Application Areas:Automotive sector｜Bottle cap｜Fitness equipment｜Communication equipment｜engineering application
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	110	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	110	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	1.6mm	IEC 60695-2-12	650	°C
UL flame retardant rating	1.6mm	UL 94	HB
Burning rate	1.00mm	FMVSS302	<100	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	380	Mpa
Bending modulus		ISO 178	15200	Mpa
Tensile strain	Break	ISO 527-2/5	2.5	%
tensile strength	Break	ISO 527-2/5	250	Mpa
Tensile modulus		ISO 527-2/1	16700	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	8.8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	1.7E-05	cm/cm/°C
Melting temperature		DIN EN11357-1	262	°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	235	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	260	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation,23°C	ISO 62	3.7to4.3	%
Shrinkage rate	MD	ISO 294-4	0.30	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.2	%
Spiral flow length		Internal Method	60.0	CM
Hygroscopicity	70°C，62%RH	ISO 1110	1.3to1.5	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+13	ohms·cm
Surface resistivity		IEC 60093	1E+12	ohms
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H961/30	ISO 2039-1	290	Mpa
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ReinforcementContent		ISO 1172	50	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 AKROMID® A3GF50 AKRO-PLASTIC GERMANY

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index