Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3GF50 AKRO-PLASTIC GERMANY
AKROMID®
Automotive sector、Bottle cap、Fitness equipment、Communication equipment、engineering application
high strength、heat-resisting、dimensional stability 、Electrical performance、Processability、Filler: Glass fiber reinf、50% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF50 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 110 kJ/m² |
| -30°C | ISO 179/1eU | 110 kJ/m² |
| hardness | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF50 |
|---|---|---|---|
| ball-indentation hardness | H961/30 | ISO 2039-1 | 290 Mpa |
| Supplementary Information | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF50 |
|---|---|---|---|
| ReinforcementContent | ISO 1172 | 50 % |
| Electrical performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF50 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+12 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF50 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 16700 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 250 Mpa |
| bending strength | ISO 178 | 380 Mpa | |
| Flexural modulus | ISO 178 | 15200 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.5 % |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF50 |
|---|---|---|---|
| burning rate | 1.00mm | FMVSS302 | <100 mm/min |
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF50 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.2 % |
| MD | ISO 294-4 | 0.30 % | |
| moisture absorption | 70°C，62%RH | ISO 1110 | 1.3to1.5 % |
| spiral flow length | 内部方法 | 60.0 CM | |
| Water absorption rate | 饱和,23°C | ISO 62 | 3.7to4.3 % |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF50 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 260 °C |
| melting temperature | DIN EN11357-1 | 262 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 1.7E-05 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 235 °C |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 8.8E-05 cm/cm/°C |