thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	流动	GB 1040	42 µm/m-°C
	Linear coefficient of thermal expansion	流动	ISO 11359-2	42 µm/m-°C
		Linear coefficient of thermal expansion	横向	GB 1040	49 µm/m-°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向	ISO 11359-2	59 µm/m-°C
Heat Deflection Temperature	1.8 MPa	Flatw 80104 sp=64mm; ISO 75/Af	89
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa	ASTMF1249	88
vicat		Rate B/50; ISO 306	107
	vicat		Rate B/50; ASTM D1525	108
	vicat	vicat		Equate	110
UL flame retardant rating		UL 94	V-0

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate		23°C / 50% RH; ISO 62	0.04 %
Water absorption rate	Water absorption rate	饱和	ISO 62	0.09 %
shrinkage rate	Flow	SABIC method	0.0025 - 0.0035 cm/cm
melt mass-flow rate		ASTM D1238	13
melt mass-flow rate	melt mass-flow rate		ASTM D1238	@Load 2.16 kg. Temperature 260
Compound melt index		MVR [cm^3/10 min]; ISO 1133	49.0 µm/m-°C g/10 min
Compound melt index	Compound melt index			@Load 2.16 kg. Temperature 260

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	屈服	ISO 178	35 Mpa
	tensile strength	Type I, 50 mm/min，屈服	ASTM D638	45 Mpa
		tensile strength	屈服	ISO 178	55 Mpa
		tensile strength	tensile strength	Type I, 50 mm/min，屈服	ASTM D638	58 Mpa
Elongation at break	断裂	ISO 178	30 %
Elongation at break	Elongation at break	Type I, 50 mm/min，断裂	ASTM D638	32 %
elongation at yield		ISO 178	3.8 %
elongation at yield	elongation at yield	Type I, 50 mm/min	ASTM D638	4 %
Tensile modulus		GB/T 15585-1995	5.2
Tensile modulus	Tensile modulus		1 mm/min; ISO 527	5.58
bending strength	1.3 mm/min, 50 mm span	ASTM D790	98 Mpa
bending strength	bending strength		2 mm/min; ISO 178	99 Mpa
flexural modulus	1.3 mm/min, 50 mm span	ASTM D790	4.53
flexural modulus	flexural modulus		2 mm/min; ISO 178	4.58
Impact strength of cantilever beam gap		ASTM D256	0.69 J/cm
	Impact strength of cantilever beam gap		ASTM D256	0.55 J/cm
		Impact strength of cantilever beam gap			@Temperature -30.0
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		80104; ISO 180/1A	5 kJ/m²
Charpy Notched Impact Strength		Edgew 80104 sp=62mm; ISO 179/1eA	0.5 J/cm²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.