PC/ABS C7230P BK1C304L SABIC INNOVATIVE NANSHA
CYCOLOY™ 
Electronic and electrical accessories,Casters,Household appliances
Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/C7230P BK1C304L
Hot deformation temperature1.8 MPaFlatw 80*10*4 sp=64mm; ISO 75/Af89
1.8 MPaASTMF124988
Linear coefficient of thermal expansionFlowGB 104042 µm/m-°C
Across FlowGB 104049 µm/m-°C
FlowISO 11359-242 µm/m-°C
Across FlowISO 11359-259 µm/m-°C
UL flame retardant ratingUL 94V-0
Vicat softening temperatureEquate110
Rate B/50; ASTM D1525108
Rate B/50; ISO 306107
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/C7230P BK1C304L
Bending modulus1.3 mm/min, 50 mm spanASTM D7904.53
2 mm/min; ISO 1784.58
bending strength1.3 mm/min, 50 mm spanASTM D79098 Mpa
2 mm/min; ISO 17899 Mpa
Charpy Notched Impact StrengthEdgew 80*10*4 sp=62mm; ISO 179/1eA0.5 J/cm²
Elongation at BreakBreakISO 17830 %
Type I, 50 mm/min，BreakASTM D63832 %
elongation at yieldType I, 50 mm/minASTM D6384 %
ISO 1783.8 %
Impact strength of cantilever beam gap@Temperature -30.0
ASTM D2560.69 J/cm
80*10*4; ISO 180/1A5 kJ/m²
Tensile modulusGB/T 15585-19955.2
1 mm/min; ISO 5275.58
tensile strengthYieldISO 17835 Mpa
Type I, 50 mm/min，YieldASTM D63845 Mpa
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/C7230P BK1C304L
Compound melt indexMVR [cm^3/10 min]; ISO 113349.0 µm/m-°C g/10 min
@Load 2.16 kg. Temperature 260
melt mass-flow rateASTM D123813
Shrinkage rateFlowSABIC method0.0025 - 0.0035 cm/cm
Water absorption rateSaturationISO 620.09 %
23°C / 50% RH; ISO 620.04 %