Material Properties:wear resistant｜high strength｜High impact resistance｜High temperature resistance｜ High impact
Application Areas:Automotive components
Color:--
Grade:Transparent level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		ASTM D-955	0.4-0.7 %
melt mass-flow rate		ASTM D624	2.0 g/10min

Mechanical properties	Test Method	Test Result
Rockwell hardness	ASTM D-785	105
bending strength	ASTM D-790	630(62) kg/cm2(MPa)
Tension measurement	ASTM D-638	17800(1740) kg/cm2(MPa)
Stretching rate (resistance point)	ASTM D-638	≥6 %
Stretching rate (breaking point)	ASTM D-638	50 %
Tensile strength	ASTM D-638	430(42) kg/cm2(MPa)
Bending modulus	ASTM D-790	20500（2000） kg/cm2(MPa)
Impact strength of cantilever beam gap	ASTM D-256	15(150) kg.cm/cm(J/m)

Thermal performance	Test Method	Test Result
combustibility	IEC 707	- mm/min
Heat distortion temperature	ASTM D-648	89(88) °C
combustibility	UL -94	HB CLASS
vicat	ASTM D-1525	98(93) °C
Heat distortion temperature	ASTM D-648	95(90) °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.