Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS TR-557I LG CHEM KOREA
--
Automotive components
wear resistant、high strength、High impact resistance、High temperature resistan、 High impact
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/TR-557I |
|---|---|---|---|
| bending strength | 15mm/min | ASTM D-790 | 630(62) kg/cm2(MPa) |
| Tensile strength | 50mm/min | ASTM D-638 | 430(42) kg/cm2(MPa) |
| Rockwell Hardness | R-Scale | ASTM D-785 | 105 |
| Bending modulus | 15mm/min | ASTM D-790 | 20500（2000） kg/cm2(MPa) |
| Tension measurement | 1mm/min | ASTM D-638 | 17800(1740) kg/cm2(MPa) |
| Stretching rate (resistance point) | 50mm/min | ASTM D-638 | ≥6 % |
| IZOD impact strength | 1/4",23°C | ASTM D-256 | 15(150) kg.cm/cm(J/m) |
| Stretching rate (breaking point) | 50mm/min | ASTM D-638 | 50 % |
| physical property | Test Condition | Test Method | LG CHEM KOREA/TR-557I |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.4～0.7 % | |
| melt mass-flow rate | 200°C/5kg | ASTM D624 | 2.0 g/10min |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/TR-557I |
|---|---|---|---|
| Flammability | 1/8" | UL-94 | HB CLASS |
| Heat Deflection Temperature | 4.6kg/cm21/4"annealed(unannealed) | ASTM D-648 | 95(90) °C |
| Hot deformation temperature | 1.86kgf/cm21/4 | ASTM D-648 | 89(88) °C |
| Flammability | 1/8" | IEC707 | - mm/min |
| Microcard softening point | 1kg/120℃/h(5kg/50℃/h) | ASTM D-1525 | 98(93) °C |