EPE ELITE™ 5100G DOW USA
240
- Unit Price:US$ 1,421 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:40MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Thin film grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 0.85 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D2457 | 33 | |
| Haze ratio | ASTM D1003 | 20 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D882 | 12.4 Mpa | |
| ASTM D882 | 43.6 Mpa | ||
| ASTM D882 | 36.0 Mpa | ||
| elongation | ASTM D882 | 480 % | |
| ASTM D882 | 620 % | ||
| Dart impact | ASTM D1709A | 540 g | |
| Elmendorf tear strength | ASTM D1922 | 260 g | |
| ASTM D1922 | 670 g | ||
| film thickness | 25 µm | ||
| Thin film puncture strength | 内部方法 | 5.76 J | |
| 内部方法 | 64.5 N | ||
| 内部方法 | 28.3 J/cm³ | ||
| film strength | ASTM D882 | 98.5 J/cm³ | |
| ASTM D882 | 98.5 J/cm³ | ||
| Secant modulus | ASTM D882 | 272 Mpa | |
| ASTM D882 | 231 Mpa | ||
| ASTM D882 | 309 Mpa | ||
| ASTM D882 | 256 Mpa | ||
| tensile strength | ASTM D882 | 11.9 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D1525 | 106 °C | |
| melting temperature | 内部方法 | 123 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.