Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EPE 5100G DOW USA
ELITE™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | DOW USA/5100G |
|---|---|---|---|
| film strength | MD | ASTM D882 | 98.5 J/cm³ |
| Secant modulus | 2%正割,TD | ASTM D882 | 256 Mpa |
| Thin film puncture strength | 内部方法 | 5.76 J | |
| Secant modulus | 1%正割,TD | ASTM D882 | 309 Mpa |
| elongation | MD:断裂 | ASTM D882 | 480 % |
| tensile strength | MD:屈服 | ASTM D882 | 11.9 Mpa |
| Dart impact | ASTM D1709A | 540 g | |
| Thin film puncture strength | 内部方法 | 28.3 J/cm³ | |
| tensile strength | TD:屈服 | ASTM D882 | 12.4 Mpa |
| Thin film puncture strength | 内部方法 | 64.5 N | |
| Elmendorf tear strength | MD | ASTM D1922 | 260 g |
| tensile strength | MD:断裂 | ASTM D882 | 43.6 Mpa |
| film thickness | 25 µm | ||
| tensile strength | TD:断裂 | ASTM D882 | 36.0 Mpa |
| Elmendorf tear strength | TD | ASTM D1922 | 670 g |
| film strength | TD | ASTM D882 | 98.5 J/cm³ |
| Secant modulus | 2%正割,MD | ASTM D882 | 231 Mpa |
| 1%正割,MD | ASTM D882 | 272 Mpa | |
| elongation | TD:断裂 | ASTM D882 | 620 % |
| optical performance | Test Condition | Test Method | DOW USA/5100G |
|---|---|---|---|
| gloss | 45° | ASTM D2457 | 33 |
| Haze ratio | ASTM D1003 | 20 % |
| physical property | Test Condition | Test Method | DOW USA/5100G |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.85 g/10min |
| Thermal performance | Test Condition | Test Method | DOW USA/5100G |
|---|---|---|---|
| vicat | ASTM D1525 | 106 °C | |
| melting temperature | 内部方法 | 123 °C |