thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8 MPa, 未退火	ISO 75-2/A	250 °C
melting temperature		DSC	265 °C
Linear coefficient of thermal expansion	流动	ISO 11359-2	2.4E-5 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	横向流量 : 3.00 mm	内部方法	0.90 %
shrinkage rate	shrinkage rate	流量 : 3.00 mm	内部方法	0.30 %
Water absorption rate	平衡, 23°C, 50% RH		2.0 %
PV Limit - vs. S45C		Suzuki Method	2.3 MPa·m/s

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		IEC 60093	0.020 ohms·cm

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	23°C	ISO 527-2	223 Mpa
Tensile strain	断裂, 23°C	ISO 527-2	2.1 %
flexural modulus	23°C	ISO 178	13800 Mpa
bending strength	23°C	ISO 178	310 Mpa
Amount of Wear - vs. S45C		Suzuki Method	0.700 mg/hr
Friction coefficient - vs. S45C		Suzuki Method	0.32

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App