PA66 3101T-20V TORAY JAPAN
Amilan®
Automotive Applications,Electrical components
Thermal stability,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/3101T-20V |
|---|---|---|---|
| Friction coefficient - vs. S45C | Suzuki Method | 0.32 | |
| Tensile strain | 断裂, 23°C | ISO 527-2 | 2.1 % |
| bending strength | 23°C | ISO 178 | 310 Mpa |
| Amount of Wear - vs. S45C | Suzuki Method | 0.700 mg/hr | |
| Flexural modulus | 23°C | ISO 178 | 13800 Mpa |
| tensile strength | 23°C | ISO 527-2 | 223 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/3101T-20V |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 0.020 ohms·cm |
| flammability | Test Condition | Test Method | TORAY JAPAN/3101T-20V |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/3101T-20V |
|---|---|---|---|
| Shrinkage rate | 流量 : 3.00 mm | 内部方法 | 0.30 % |
| 横向流量 : 3.00 mm | 内部方法 | 0.90 % | |
| Water absorption rate | 平衡, 23°C, 50% RH | 2.0 % | |
| PV Limit - vs. S45C | Suzuki Method | 2.3 MPa·m/s |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/3101T-20V |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 250 °C |
| melting temperature | DSC | 265 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 2.4E-5 cm/cm/°C |