PBT Toraycon® 1101G-X50 TORAY JAPAN
224
- Unit Price:US$ 3,149 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:40MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Flame retardant｜High impact resistance
- Application Areas:Automotive sector｜Electronic field｜Electrical field
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 91 M（Scale） |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa未退火 | ISO 75-2/Bf | 220 °C |
| 1.80MPa退火 | ISO 75-2/Af | 208 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4.2E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa | ASTM D648 | 220 °C |
| 1.82Mpa | ASTM D648 | 212 °C | |
| Linear coefficient of thermal expansion | ASTM D696 | 2.0 | |
| UL flame retardant rating | UL 94 | HB | |
| Combustibility (rate) | UL 94 | HB | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 212 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 2.0x10^-5 mm/mm.℃ |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 填充增强级.低翘曲 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB - |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | 4.6E+16 Ω.cm | |
| dielectric strength | IEC 60243-1 | 23 KV/mm | |
| dielectric constant | 23°C | IEC 60250 | 3.50 1MHz |
| Dissipation Factor | 23°C | IEC 60250 | 0.010 1MHz |
| 耐电弧性 | IEC 61621 | 137 S | |
| volume resistivity | ASTM D495 | 137 S | |
| ASTM D257 | 2.3 | ||
| dielectric strength | ASTM D149 | 23 MV/m | |
| dielectric constant | 50Hz | ASTM D150 | 3.5 |
| 10 | ASTM D150 | 3.5 | |
| Dielectric loss | 50Hz，正切 | ASTM D150 | 0.002 |
| 10，正切 | ASTM D150 | 0.01 | |
| dielectric constant | ASTM D150/IEC 60250 | 3.5 | |
| volume resistivity | ASTM D257/IEC 60093 | 2.3x10^14 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD | ISO 294-4 | 0.20 % |
| TD | ISO 294-4 | 0.80 % | |
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.070 % |
| 23℃,24hr | ASTM D570 | 0.07 % | |
| density | ASTM D792/ISO 1183 | 1.55 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.07 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 23°C | ISO 527-2 | 140 Mpa |
| Elongation at break | 23°C | ISO 527-2 | 2.5 % |
| Tensile modulus | 23°C | ISO 527-2 | 10500 Mpa |
| bending strength | 23°C | ISO 178 | 220 Mpa |
| flexural modulus | 23°C | ISO 178 | 9700 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| tensile strength | 23℃ | ASTM D638 | 140 Mpa |
| elongation | 23℃ | ASTM D638 | 4 % |
| bending strength | 23℃ | ASTM D790 | 205 Mpa |
| flexural modulus | 23℃ | ASTM D790 | 8.8 GPa |
| Impact strength of cantilever beam gap | 缺口，23℃ | ASTM D256 | 70 J/m |
| 缺口，-40℃ | ASTM D256 | 60 J/m | |
| 无缺口，23℃ | ASTM D256 | 40 KJ/m | |
| 无缺口，-40℃ | ASTM D256 | 25 KJ/m | |
| Rockwell hardness | ASTM D785 | 93 M | |
| coefficient of friction | 对本身 | ASTM D1894 | 0.15 |
| 对金属 | ASTM D1894 | 0.19 | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 70 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 60 kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 40 kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 25 kg·cm/cm(J/M)ft·lb/in | ||
| Elongation at break | ASTM D638/ISO 527 | 4 % | |
| tensile strength | ASTM D638/ISO 527 | 140 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | M93 | |
| flexural modulus | ASTM D790/ISO 178 | 8800 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 205 kg/cm²(MPa)[Lb/in²] |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.