Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PBT 1101G-X50 TORAY JAPAN
Toraycon®
Automotive sector,Electronic field,Electrical field
Glass fiber reinforced,Flame retardant,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | TORAY JAPAN/1101G-X50 |
---|---|---|---|
Rockwell hardness | ISO 2039-2 | 91 M(Scale) |
Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1101G-X50 |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 25 kg·cm/cm(J/M)ft·lb/in | |
bending strength | ASTM D790/ISO 178 | 205 kg/cm²(MPa)[Lb/in²] | |
Flexural modulus | ASTM D790/ISO 178 | 8800 kg/cm²(MPa)[Lb/in²] | |
Rockwell hardness | ASTM D785 | 93 M | |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
Tensile modulus | 23°C | ISO 527-2 | 10500 Mpa |
elongation at break | ASTM D638/ISO 527 | 4 % | |
bending strength | 23℃ | ASTM D790 | 205 Mpa |
Flexural modulus | 23℃ | ASTM D790 | 8.8 GPa |
Rockwell hardness | ASTM D785 | M93 | |
tensile strength | ASTM D638/ISO 527 | 140 kg/cm²(MPa)[Lb/in²] | |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
coefficient of friction | 对本身 | ASTM D1894 | 0.15 |
elongation | 23℃ | ASTM D638 | 4 % |
bending strength | 23°C | ISO 178 | 220 Mpa |
Flexural modulus | 23°C | ISO 178 | 9700 Mpa |
Impact strength of cantilever beam gap | 无缺口,-40℃ | ASTM D256 | 25 KJ/m |
tensile strength | 23℃ | ASTM D638 | 140 Mpa |
elongation at break | 23°C | ISO 527-2 | 2.5 % |
Impact strength of cantilever beam gap | 缺口,23℃ | ASTM D256 | 70 J/m |
缺口,-40℃ | ASTM D256 | 60 J/m | |
coefficient of friction | 对金属 | ASTM D1894 | 0.19 |
tensile strength | 23°C | ISO 527-2 | 140 Mpa |
Impact strength of cantilever beam gap | 无缺口,23℃ | ASTM D256 | 40 KJ/m |
Electrical performance | Test Condition | Test Method | TORAY JAPAN/1101G-X50 |
---|---|---|---|
dielectric constant | 50Hz | ASTM D150 | 3.5 |
Dielectric loss | 10,正切 | ASTM D150 | 0.01 |
dielectric strength | ASTM D149 | 23 MV/m | |
dielectric constant | ASTM D150/IEC 60250 | 3.5 | |
Dissipation Factor | 23°C | IEC 60250 | 0.010 1MHz |
Dielectric loss | 50Hz,正切 | ASTM D150 | 0.002 |
Volume resistivity | ASTM D257/IEC 60093 | 2.3x10^14 Ω.cm | |
IEC 60093 | 4.6E+16 Ω.cm | ||
Dissipation Factor | 耐电弧性 | IEC 61621 | 137 S |
Volume resistivity | ASTM D495 | 137 S | |
dielectric strength | IEC 60243-1 | 23 KV/mm | |
dielectric constant | 23°C | IEC 60250 | 3.50 1MHz |
10 | ASTM D150 | 3.5 | |
Volume resistivity | ASTM D257 | 2.3 |
other | Test Condition | Test Method | TORAY JAPAN/1101G-X50 |
---|---|---|---|
characteristic | 填充增强级.低翘曲 |
Physical properties | Test Condition | Test Method | TORAY JAPAN/1101G-X50 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1.55 | |
Water absorption rate | ASTM D570/ISO 62 | 0.07 % |
flammability | Test Condition | Test Method | TORAY JAPAN/1101G-X50 |
---|---|---|---|
UL flame retardant rating | UL -94 | HB - |
physical property | Test Condition | Test Method | TORAY JAPAN/1101G-X50 |
---|---|---|---|
Water absorption rate | (23°C,24hr) | ISO 62 | 0.070 % |
Shrinkage rate | TD | ISO 294-4 | 0.80 % |
MD | ISO 294-4 | 0.20 % | |
Water absorption rate | 23℃,24hr | ASTM D570 | 0.07 % |
Thermal performance | Test Condition | Test Method | TORAY JAPAN/1101G-X50 |
---|---|---|---|
Combustibility (rate) | UL 94 | HB | |
Heat distortion temperature | 1.80MPa退火,HDT | ISO 75-2/Af | 208 °C |
0.45MPa,HDT | ASTM D648 | 220 °C | |
HDT | ASTM D648/ISO 75 | 212 ℃(℉) | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4.2E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa未退火,HDT | ISO 75-2/Bf | 220 °C |
1.82Mpa,HDT | ASTM D648 | 212 °C | |
Linear coefficient of thermal expansion | ASTM D696 | 2.0 | |
ASTM D696/ISO 11359 | 2.0x10^-5 mm/mm.℃ | ||
UL flame retardant rating | UL 94 | HB |