TPV

TPV Santoprene™ 101-73 CELANESE USA

367
  • Unit Price:US$ 4,483 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    125MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High temperature resistance｜Aging resistance｜Flame retardant
  • Application Areas:Fitness equipment｜Automotive Applications｜Electrical applications｜Application in the automotive field｜packing｜Pipe fittings｜Home appliance components｜Consumer product application field｜Parts under the hood of a car｜Outdoor applications｜Washer｜Electrical components｜diaphragm
  • Color:--
  • Grade:Injection grade

Technical Data Sheet Compare

hardnessTest ConditionTest MethodTest Result
Shore hardness邵氏A,15秒,23°CISO 86878
thermal performanceTest ConditionTest MethodTest Result
brittle temperatureASTM D746-60.0 °C
brittle temperatureISO 812-60.0 °C
RTI ElecUL 74690.0 °C
RTI Str1.0mmUL 74690.0 °C
RTI Str1.5mmUL 74690.0 °C
RTI Str3.0mmUL 74695.0 °C
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.0mmUL 94HB
UL flame retardant rating1.5mmUL 94HB
UL flame retardant rating3.0mmUL 94HB
elastomerTest ConditionTest MethodTest Result
Tensile stress100%应变,23°C，横向流量ASTM D4123.60 Mpa
Tensile stress100%应变,23°C，横向流量ISO 373.60 Mpa
tensile strength断裂,23°C，横向流量ASTM D4128.80 Mpa
tensile strengthBreak,23°CISO 378.80 Mpa
elongation断裂,23°C，横向ASTM D412490 %
elongation断裂,23°C，横向ISO 37490 %
tear strength23°C，横向流量ASTM D62427.0 kN/m
tear strength23°C，Across Flow (横向)ISO 34-127 kN/m
compression set70°C,22hrASTM D395B28 %
compression set125°C,70hrASTM D395B37 %
compression set70°C,22hrISO 81528 %
compression set125°C,70hrISO 81537 %
agingTest ConditionTest MethodTest Result
Change rate of ultimate elongation in air23°C,168hr,inSulfuricAcid,98%ASTM D471-27 %
Change rate of ultimate elongation in air23°C,168hr,inTrichloroethyleneASTM D47122 %
Change rate of ultimate elongation in air100°C,168hr,inDeionizedWaterASTM D471-7.0 %
Change rate of ultimate elongation in air100°C,168hr,inIRM903OilASTM D471-49 %
Change rate of ultimate elongation in air125°C,70hr,inIRM903OilASTM D471-47 %
Change rate of ultimate elongation in air125°C,168hr,inIRM903OilASTM D471-58 %
Tensile stress change rate23°C,168hr,inAceticAcid，断裂ISO 1817-4.0 %
Tensile stress change rate23°C,168hr,inCyclohexane，断裂ISO 181720 %
Tensile stress change rate23°C,168hr,inDetergent(Tide),2.5%，断裂ISO 18172.0 %
Tensile stress change rate23°C,168hr,inEthanol,95%，断裂ISO 18170.0 %
Shore hardnessShoreA,23°C,168hr,inIsopropylAlcoholISO 1817-1.0
Shore hardnessShoreA,23°C,168hr,inMethylethylketoneISO 18170.0
Shore hardnessShoreA,23°C,168hr,inSodiumChloride,15%ISO 18170.0
Shore hardnessShoreA,23°C,168hr,inSodiumHydroxide,50%ISO 18170.0
Shore hardnessShoreA,23°C,168hr,inSulfuricAcid,98%ISO 18170.0
Shore hardnessShoreA,23°C,168hr,inTrichloroethyleneISO 1817-3.0
Shore hardnessShoreA,100°C,168hr,inDeionizedWaterISO 1817-2.0
Shore hardnessShoreA,100°C,168hr,inIRM903OilISO 1817-21
Shore hardnessShoreA,125°C,168hr,inIRM903OilISO 1817-23
mass change fraction23°C,168hr,inAceticAcidASTM D4714.0 %
mass change fraction23.0°C,168hr,inSodiumChloride,15%ISO 18170.20 %
mass change fraction23.0°C,168hr,inDetergent(Tide),2.5%ISO 18170.60 %
mass change fraction23.0°C,168hr,inSulfuricAcid,98%ISO 18173.6 %
mass change fraction100°C,168hr,inDeionizedWaterISO 18173.6 %
mass change fraction23.0°C,168hr,inAceticAcidISO 18174.0 %
mass change fraction100°C,168hr,inIRM903OilISO 181766 %
mass change fraction125°C,168hr,inIRM903OilISO 181778 %
volume change125°C,70hr,在IRM903油中ASTM D47172 %
volume change125°C,70hr,在IRM903油中ISO 181772 %
Shore hardnessShoreA,150°C,168hrISO 1887.0
Change rate of tensile strength in air23°C,168hr,inAceticAcidASTM D471-8.0 %
Change rate of tensile strength in air23°C,168hr,inCyclohexaneASTM D47131 %
Change rate of tensile strength in air23°C,168hr,inDetergent(Tide),2.5%ASTM D4713.0 %
Change rate of tensile strength in air23°C,168hr,inEthanol,95%ASTM D471-2.0 %
Change rate of tensile strength in air23°C,168hr,inHydrochloricAcid,10%ASTM D47113 %
Change rate of tensile strength in air23°C,168hr,inIsopropylAlcoholASTM D47131 %
Change rate of tensile strength in air23°C,168hr,inMethylethylketoneASTM D47147 %
Change rate of tensile strength in air23°C,168hr,inSodiumChloride,15%ASTM D4710.0 %
Change rate of tensile strength in air23°C,168hr,inSodiumHydroxide,50%ASTM D4713.0 %
Tensile stress change rate23°C,168hr,inHydrochloricAcid,10%，断裂ISO 18179.0 %
Tensile stress change rate23°C,168hr,inIsopropylAlcohol，断裂ISO 181720 %
Tensile stress change rate23°C,168hr,inMethylethylketone，断裂ISO 181724 %
Tensile stress change rate23°C,168hr,inSodiumChloride,15%，断裂ISO 1817-2.0 %
Tensile stress change rate23°C,168hr,inSodiumHydroxide,50%，断裂ISO 18172.0 %
Tensile stress change rate23°C,168hr,inSulfuricAcid,98%，断裂ISO 1817-27 %
Tensile stress change rate23°C,168hr,inTrichloroethylene，断裂ISO 181722 %
Tensile stress change rate100°C,168hr,inDeionizedWater，断裂ISO 1817-7.0 %
Tensile stress change rate100°C,168hr,inIRM903Oil，断裂ISO 1817-49 %
Tensile stress change rate125°C,70hr,inIRM903Oil，断裂ISO 1817-47 %
mass change fraction23°C,168hr,inCyclohexaneASTM D471-4.9 %
mass change fraction23°C,168hr,inDetergent(Tide),2.5%ASTM D4710.60 %
mass change fraction23°C,168hr,inEthanol,95%ASTM D471-0.10 %
mass change fraction23°C,168hr,inHydrochloricAcid,10%ASTM D4710.20 %
mass change fraction23°C,168hr,inIsopropylAlcoholASTM D471-13 %
mass change fraction23°C,168hr,inMethylethylketoneASTM D471-24 %
mass change fraction23°C,168hr,inSodiumChloride,15%ASTM D4710.20 %
mass change fraction23°C,168hr,inSodiumHydroxide,50%ASTM D471-0.20 %
mass change fraction23°C,168hr,inSulfuricAcid,98%ASTM D4713.6 %
mass change fraction23°C,168hr,inTrichloroethyleneASTM D471-6.0 %
mass change fraction100°C,168hr,inDeionizedWaterASTM D4713.6 %
mass change fraction100°C,168hr,inIRM903OilASTM D47166 %
mass change fraction125°C,168hr,inIRM903OilASTM D47178 %
mass change fraction23.0°C,168hr,inMethylethylketoneISO 1817-24 %
mass change fraction23.0°C,168hr,inIsopropylAlcoholISO 1817-13 %
mass change fraction23.0°C,168hr,inTrichloroethyleneISO 1817-6.0 %
mass change fraction23.0°C,168hr,inCyclohexaneISO 1817-4.9 %
mass change fraction23.0°C,168hr,inSodiumHydroxide,50%ISO 1817-0.20 %
mass change fraction23.0°C,168hr,inEthanol,95%ISO 1817-0.10 %
mass change fraction23.0°C,168hr,inHydrochloricAcid,10%ISO 18170.20 %
Change rate of tensile strength in air23°C,168hr,inHydrochloricAcid,10%ISO 181713 %
Change rate of tensile strength in air23°C,168hr,inIsopropylAlcoholISO 181731 %
Change rate of tensile strength in air23°C,168hr,inMethylethylketoneISO 181747 %
Change rate of tensile strength in air23°C,168hr,inSodiumChloride,15%ISO 18170.0 %
Change rate of tensile strength in air23°C,168hr,inSodiumHydroxide,50%ISO 18173.0 %
Change rate of tensile strength in air23°C,168hr,inSulfuricAcid,98%ISO 1817-17 %
Change rate of tensile strength in air23°C,168hr,inTrichloroethyleneISO 181754 %
Change rate of tensile strength in air100°C,168hr,inDeionizedWaterISO 18171.0 %
Change rate of tensile strength in air100°C,168hr,inIRM903OilISO 1817-30 %
Change rate of tensile strength in air125°C,70hr,inIRM903OilISO 1817-31 %
Tensile stress change rate125°C,168hr,inIRM903Oil，断裂ISO 1817-58 %
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inAceticAcidASTM D471-2.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inCyclohexaneASTM D471-16
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inDetergent(Tide),2.5%ASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inEthanol,95%ASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inHydrochloricAcid,10%ASTM D471-3.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inIsopropylAlcoholASTM D471-1.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inMethylethylketoneASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inSodiumChloride,15%ASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inSodiumHydroxide,50%ASTM D4710.0
Change rate of tensile strength in air150°C,168hrASTM D573-1.0 %
Change rate of tensile strength in air150°C,168hrISO 188-1.0 %
Change rate of ultimate elongation in air150°C,168hrASTM D573-3.0 %
Hardness change rate in the airShoreA,150°C,168hrASTM D5737.0
Change rate of tensile strength in air23°C,168hr,inSulfuricAcid,98%ASTM D471-17 %
Change rate of tensile strength in air23°C,168hr,inTrichloroethyleneASTM D47154 %
Change rate of tensile strength in air100°C,168hr,inDeionizedWaterASTM D4711.0 %
Change rate of tensile strength in air100°C,168hr,inIRM903OilASTM D471-30 %
Change rate of tensile strength in air125°C,70hr,inIRM903OilASTM D471-31 %
Change rate of tensile strength in air125°C,168hr,inIRM903OilASTM D471-31 %
Change rate of tensile strength in air23°C,168hr,inAceticAcidISO 1817-8.0 %
Change rate of tensile strength in air23°C,168hr,inCyclohexaneISO 181731 %
Change rate of tensile strength in air23°C,168hr,inDetergent(Tide),2.5%ISO 18173.0 %
Change rate of tensile strength in air23°C,168hr,inEthanol,95%ISO 1817-2.0 %
Change rate of tensile strength in air125°C,168hr,inIRM903OilISO 1817-31 %
Change rate of ultimate elongation in air23°C,168hr,inAceticAcidASTM D471-4.0 %
Change rate of ultimate elongation in air23°C,168hr,inCyclohexaneASTM D47120 %
Change rate of ultimate elongation in air23°C,168hr,inDetergent(Tide),2.5%ASTM D4712.0 %
Change rate of ultimate elongation in air23°C,168hr,inEthanol,95%ASTM D4710.0 %
Change rate of ultimate elongation in air23°C,168hr,inHydrochloricAcid,10%ASTM D4719.0 %
Change rate of ultimate elongation in air23°C,168hr,inIsopropylAlcoholASTM D47120 %
Change rate of ultimate elongation in air23°C,168hr,inMethylethylketoneASTM D47124 %
Change rate of ultimate elongation in air23°C,168hr,inSodiumChloride,15%ASTM D471-2.0 %
Change rate of ultimate elongation in air23°C,168hr,inSodiumHydroxide,50%ASTM D4712.0 %
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inSulfuricAcid,98%ASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inTrichloroethyleneASTM D471-3.0
Change rate of hardness (Shore) in the airShoreA,100°C,168hr,inDeionizedWaterASTM D471-2.0
Change rate of hardness (Shore) in the airShoreA,100°C,168hr,inIRM903OilASTM D471-21
Change rate of hardness (Shore) in the airShoreA,125°C,168hr,inIRM903OilASTM D471-23
Shore hardnessShoreA,23°C,168hr,inAceticAcidISO 1817-2.0
Shore hardnessShoreA,23°C,168hr,inCyclohexaneISO 1817-16
Shore hardnessShoreA,23°C,168hr,inDetergent(Tide),2.5%ISO 18170.0
Shore hardnessShoreA,23°C,168hr,inEthanol,95%ISO 18170.0
Shore hardnessShoreA,23°C,168hr,inHydrochloricAcid,10%ISO 1817-3.0
Physical propertiesTest ConditionTest MethodTest Result
Outdoor applicabilityUL 746Cf1
Resistance to cleaning agentsISO 188f4
Resistance to cleaning agentsUL 749f3
Electrical performanceTest ConditionTest MethodTest Result
dielectric strength23°C,2.00mmASTM D14927 KV/mm
dielectric constant23°C,1.98mmASTM D1502.50
dielectric constant23°C,1.98mmIEC 602502.50
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 0
High arc combustion index (HAI)HAIUL 746PLC 0
High Voltage Arc Traceability Rate (HVTR)PLCUL 746
High Voltage Arc Traceability Rate (HVTR)HVTRUL 746PLC 1
Hot wire ignition (HWI)1.0mmUL 746PLC 4
Hot wire ignition (HWI)1.5mmUL 746PLC 3
Hot wire ignition (HWI)3.0mmUL 746PLC 3
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.