PPO/PA

PPO/PA NORYL GTX™ GTX675-74709 SABIC INNOVATIVE US

353

Unit Price:US$ 4,740 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
65MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Hydrolysis resistance｜High temperature resistance｜Dimensional stability｜High mobility
Application Areas:Industrial machinery｜Electrical applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	12 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	5.00 J

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break3	ASTM D638	6.1 %
elongation	elongation	Break	ISO 527-2/50	7.1 %
Bending modulus	50.0mmSpan4	ASTM D790	2520 Mpa
Bending modulus	Bending modulus	--5	ISO 178	2470 Mpa
bending strength	--5,6	ISO 178	103 Mpa
bending strength	bending strength	Yield,50.0mmSpan4	ASTM D790	100 Mpa
Tensile modulus	--2	ASTM D638	2420 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2670 Mpa
tensile strength	Yield3	ASTM D638	65.0 Mpa
	tensile strength	Yield	ISO 527-2/50	66.0 Mpa
		tensile strength	Break3	ASTM D638	63.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	64.0 Mpa
elongation	Yield3	ASTM D638	3.8 %
elongation	elongation	Yield	ISO 527-2/50	4.0 %

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	8.6E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	187 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan9	ISO 75-2/Bf	184 °C
Vicat softening temperature	--	ASTMD152510	197 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	198 °C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7.6E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	8.1E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	7.8E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/5.0kg	ASTM D1238	7.8 g/10min
Melt Volume Flow Rate (MVR)	300°C/5.0kg	ISO 1133	7.00 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	1.3-1.5 %
Water absorption rate	Saturation,23°C	ISO 62	4.0 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.40 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		Internal Method	1.0E+3-1.0E+4 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO/PA NORYL GTX™ GTX675-74709 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet