Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO/PA GTX675-74709 SABIC INNOVATIVE US
NORYL GTX™
Industrial machinery、Electrical applications
Hydrolysis resistance、High temperature resistan、Dimensional stability、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX675-74709 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 5.00 J |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX675-74709 |
|---|---|---|---|
| Volume resistivity | 内部方法 | 1.0E+3-1.0E+4 ohms·cm |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/GTX675-74709 |
|---|---|---|---|
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 100 Mpa |
| Tensile modulus | --2 | ASTM D638 | 2420 Mpa |
| elongation | 断裂3 | ASTM D638 | 6.1 % |
| tensile strength | 屈服3 | ASTM D638 | 65.0 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 7.1 % |
| Flexural modulus | --5 | ISO 178 | 2470 Mpa |
| 50.0mm跨距4 | ASTM D790 | 2520 Mpa | |
| bending strength | --5,6 | ISO 178 | 103 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 64.0 Mpa |
| 屈服 | ISO 527-2/50 | 66.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 4.0 % |
| 屈服3 | ASTM D638 | 3.8 % | |
| tensile strength | 断裂3 | ASTM D638 | 63.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2670 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/GTX675-74709 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.3-1.5 % |
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 7.00 cm3/10min |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 7.8 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.40 % |
| 饱和,23°C | ISO 62 | 4.0 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX675-74709 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,64.0mm跨距9，HDT | ISO 75-2/Bf | 184 °C |
| vicat | -- | ISO 306/B120 | 198 °C |
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 8.6E-05 cm/cm/°C |
| MD:23到60°C | ISO 11359-2 | 8.1E-05 cm/cm/°C | |
| TD:-40到40°C | ASTME831 | 7.8E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 187 °C |
| vicat | -- | ASTMD152510 | 197 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7.6E-05 cm/cm/°C |