PA12 UBESTA 3030JI5L UBE JAPAN
290
- Unit Price:US$ 12,486 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Good flexibility｜High impact resistance｜heat-resisting｜Toughening
- Application Areas:Pipe fittings｜Automotive sector｜Pipe fittings
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 51 |
| Shore hardness | 邵氏D | ISO 868 | 67 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45Mpa | ISO 75-2 | 91 °C |
| 1.8Mpa | ISO 75-2 | 45 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.7 | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 91 ℃（℉） |
| HDT | ASTM D648/ISO 75 | 45 ℃（℉） | |
| melting temperature | 173 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.7 mm/mm.℃ | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 91.0 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 45.0 °C | |
| melting temperature | ISO 3146 | 173 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.7E-04 cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | ISO 294-4 | 0.7/1.4 % | |
| Water absorption rate | ISO 62 | 0.6 % | |
| melt mass-flow rate | ISO 1133 | 4 g/10min | |
| melting temperature | ISO 11357-3 | 173 °C | |
| density | ASTM D792/ISO 1183 | 1.01 kg·cm/cm(J/M)ft·lb/in | |
| shrinkage rate | ASTM D955 | 0.7/1.4 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 4 g/10min | |
| 235°C/2.16kg | ISO 1133 | 4.0 g/10min | |
| shrinkage rate | TD | ISO 294-4 | 1.4 % |
| MD | ISO 294-4 | 0.70 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.60 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | 10 Ω.cm | |
| ASTM D257/IEC 60093 | 1012 Ω.cm | ||
| IEC 60093 | 1E+12 ohms·cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-1/-2 | 26 Mpa |
| elongation | 断裂 | ISO 527-1/-2 | ＞200 % |
| bending strength | ISO 178 | 19 Mpa | |
| flexural modulus | ISO 178 | 400 Mpa | |
| Shore hardness | ISO 868 | 67 D | |
| Rockwell hardness | ISO 2039-2 | 51 R | |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 115P KJ/m |
| -40℃ | ISO 179/1eA | 4C KJ/m | |
| Elongation at break | ASTM D412/ISO 527 | ＞200 % | |
| tensile strength | ASTM D412/ISO 527 | 26 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 51 | |
| flexural modulus | ASTM D412/ISO 527 | 400 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 19 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ISO 178 | 400 Mpa | |
| bending strength | ISO 178 | 19.0 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 26.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 24 % |
| 断裂 | ISO 527-2 | 200 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.