Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12 3030JI5L UBE JAPAN
UBESTA
Pipe fittings、Automotive sector、Pipe fittings
Good flexibility、High impact resistance、heat-resisting、Toughening
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UBE JAPAN/3030JI5L |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 67 |
| Rockwell hardness | R计秤 | ISO 2039-2 | 51 |
| Mechanical properties | Test Condition | Test Method | UBE JAPAN/3030JI5L |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 19 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D412/ISO 527 | ＞200 % | |
| tensile strength | ASTM D412/ISO 527 | 26 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 屈服 | ISO 527-2 | 24 % |
| Rockwell hardness | ASTM D785 | 51 | |
| tensile strength | 屈服 | ISO 527-1/-2 | 26 Mpa |
| elongation | 断裂 | ISO 527-1/-2 | ＞200 % |
| bending strength | ISO 178 | 19.0 Mpa | |
| Flexural modulus | ISO 178 | 400 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 200 % |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 115P KJ/m |
| -40℃ | ISO 179/1eA | 4C KJ/m | |
| Flexural modulus | ASTM D412/ISO 527 | 400 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ISO 2039-2 | 51 R | |
| tensile strength | 屈服 | ISO 527-2 | 26.0 Mpa |
| Shore hardness | ISO 868 | 67 D |
| Electrical performance | Test Condition | Test Method | UBE JAPAN/3030JI5L |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+12 ohms·cm | |
| ASTM D257/IEC 60093 | 1012 Ω.cm | ||
| IEC 60093 | 10 Ω.cm |
| Physical properties | Test Condition | Test Method | UBE JAPAN/3030JI5L |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.7/1.4 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 4 g/10min | |
| density | ASTM D792/ISO 1183 | 1.01 kg·cm/cm(J/M)ft·lb/in |
| physical property | Test Condition | Test Method | UBE JAPAN/3030JI5L |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.6 % | |
| Shrinkage rate | TD | ISO 294-4 | 1.4 % |
| MD | ISO 294-4 | 0.70 % | |
| ISO 294-4 | 0.7/1.4 % | ||
| melt mass-flow rate | ISO 1133 | 4 g/10min | |
| 235°C/2.16kg | ISO 1133 | 4.0 g/10min | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.60 % |
| melting temperature | ISO 11357-3 | 173 °C |
| Thermal performance | Test Condition | Test Method | UBE JAPAN/3030JI5L |
|---|---|---|---|
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.7 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 45 ℃（℉） |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 91.0 °C | |
| 1.8Mpa，HDT | ISO 75-2 | 45 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 45.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.7E-04 cm/cm/°C |
| Heat distortion temperature | 0.45Mpa，HDT | ISO 75-2 | 91 °C |
| melting temperature | 173 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.7 mm/mm.℃ | |
| melting temperature | ISO 3146 | 173 °C |