PA66 A216V15 SOLVAY SHANGHAI

291

Unit Price:US$ 3,593 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:dimensional stability ｜High mobility
Application Areas:Industrial applications｜Electrical field｜Electronic field｜Household appliances｜Household appliances｜Pulley｜Laptop case｜Engine parts
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ISO 4589-2	26 %
Ignition temperature of heating wire	1.6mm	IEC 60695-2-13	650 °C
Burning wire flammability index	0.8mm	IEC 60695-2-12	650 °C
UL flame retardant rating	3.2mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break,23°C	ISO 527-2	>30 %
elongation	Break,23°C	ASTM D638	30 %
Tensile strain	Yield,23°C	ISO 527-2	4.5 %
tensile strength	Break,23°C	ISO 527-2/1A	55.0 Mpa
	tensile strength	Yield,23°C	ISO 527-2/1A	85.0 Mpa
	tensile strength	tensile strength	Yield,23°C	ASTM D638	85.0 Mpa
Tensile modulus	23°C	ISO 527-2/1A	3200 Mpa
Bending modulus	23°C	ASTM D790	3000 Mpa
Bending modulus	Bending modulus	23°C	ISO 178	2800 Mpa
bending strength	23°C	ASTM D790	125 Mpa
bending strength	bending strength	23°C	ISO 178	120 Mpa

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 11357-3	263 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	75.0 °C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	200 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	220 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.9 %
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	1.3 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 1
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Dissipation factor		IEC 60250	0.030
Relative permittivity		IEC 60250	2.90
Dielectric strength	2.00mm	IEC 60243-1	25 KV/mm
Volume resistivity		IEC 60093	1E+15 ohms·cm
Surface resistivity		IEC 60093	1E+15 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 A216V15 SOLVAY SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet