ABS

ABS XG569C LG CHEM KOREA

237

Unit Price:US$ 2,642 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
25.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS XG-569C LG GUANGZHOU

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High gloss｜scratch resistance
Application Areas:Electrical enclosure｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C, 3.20 mm, Injection	ASTM D790	96.0 Mpa
Bending modulus	23°C, 3.20 mm, Injection	ASTM D790	2850 Mpa
elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	> 15 %
tensile strength	Yield, 23°C, 3.20 mm, Injection	ASTM D638	59.0 Mpa
Tensile modulus	23°C, 3.20 mm, Injection	ASTM D638	2650 Mpa

injection	Test Condition	Test Method	Test Result
Screw speed			30 to 60 rpm
Back pressure			2.94 to 5.88 Mpa
Mold temperature			40 to 60 °C
Processing (melt) temperature			200 to 230 °C
Spray nozzle temperature			200 to 230 °C
Temperature at the front of the material cylinder			200 to 220 °C
Temperature in the middle of the barrel			190 to 210 °C
Temperature at the rear of the barrel			180 to 200 °C
drying time			3.0 to 4.0 hr
drying temperature			80 to 90 °C

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	50.0 °C
RTI Imp		UL 746	50.0 °C
RTI Elec		UL 746	50.0 °C
Vicat softening temperature		ASTM D15257	92.0 °C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	84.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	23°C, 3.20 mm, Injection，Flow	ASTM D955	0.40 - 0.70 %
melt mass-flow rate	220°C/10.0 kg	ASTM D1238	11 g/10 min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale, 23°C, Injection	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS XG569C LG CHEM KOREA

Material Description

Technical Data Sheet Compare

Technical Data Sheet