POM LNP™ LUBRICOMP™ KFL-4416 SABIC INNOVATIVE US

329

Unit Price:US$ 3,680 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜UV resistance
Application Areas:Casters｜household electrical appliances
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Energy at Peak	ASTM D3763	9.00	J
Dart impact	Dart impact	--	ISO 6603-2	2.00	J
Suspended wall beam without notch impact strength	23°C3	ISO 180/1U	17	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	210	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear factor		ASTM D3702	1.9E+8	10^-8 mm³/N·m
Friction coefficient	Static	ASTM D3702	0.43
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702	0.50
bending strength		ASTM D790	92.0	Mpa
Bending modulus	--	ISO 178	6300	Mpa
Bending modulus	Bending modulus	--	ASTM D790	5300	Mpa
elongation	Break	ISO 527-2	4.0	%
	elongation	Break	ASTM D638	2.6	%
		elongation	Yield	ISO 527-2	2.3	%
		elongation	elongation	Yield	ASTM D638	3.6	%
tensile strength	Break	ISO 527-2	46.0	Mpa
	tensile strength	Break	ASTM D638	56.0	Mpa
		tensile strength	Yield	ISO 527-2	49.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	56.0	Mpa
Tensile modulus	--	ISO 527-2/1	5800	Mpa
Tensile modulus	Tensile modulus	--1	ASTM D638	6130	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
drying time			4.0	hr
Temperature at the rear of the barrel			175 to 190	°C
Temperature in the middle of the barrel			195 to 205	°C
Temperature at the front of the material cylinder			210 to 220	°C
Processing (melt) temperature			200 to 215	°C
Mold temperature			80 to 110	°C
Back pressure			0.200 to 0.300	Mpa
Screw speed			30 to 60	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	161	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	132	°C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span3	ISO 75-2/Af	147	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.29	%
Water absorption rate	Water absorption rate	24 hr, 50% RH	ASTM D570	0.16	%
Shrinkage rate	Flow : 24hr	ISO 294-4	1.5	%
	Shrinkage rate	横向Flow : 24hr	ISO 294-4	1.3	%
		Shrinkage rate	Across FlowFlow : 24hr	ASTM D955	1.6	%
		Shrinkage rate	Shrinkage rate	Flow : 24hr	ASTM D955	1.4	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

POM LNP™ LUBRICOMP™ KFL-4416 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index