PA6 Durethan® BKV215H2.0 LANXESS GERMANY

274

Unit Price:US$ 2,931 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
106.8MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Apparent density		ISO 60	0.60 g/cm³
Shrinkage rate		ISO 2577	0.61 %
	Shrinkage rate		ISO 2577	0.15 %
		Shrinkage rate		ISO 2577	0.59 %
		Shrinkage rate	Shrinkage rate		ISO 2577	0.14 %
Water absorption rate		ISO 62	7.0 %
Water absorption rate	Water absorption rate		ISO 62	2.0 %

hardness	Test Condition	Test Method	Test Result
ball-indentation hardness		ISO 2039-1	110 Mpa

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
Burning wire flammability index		IEC 60695-2-12	650 °C
Limiting Oxygen Index		ISO 4589-2	22 %
Burning Behavior		ISO 3795	passed

Supplementary Information	Test Condition	Test Method	Test Result
ISO Shortcut		ISO 1874	PA6/66HI.GR.14-040.GF15

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	4500 Mpa
tensile strength		ISO 527-2/5	85.0 Mpa
Tensile strain		ISO 527-2/5	4.5 %
Flexural modulus		ISO 178/A	4000 Mpa
bending strength		ISO 178/A	125 Mpa
bending strength	bending strength		ISO 178/A	130 Mpa
Bending Strain		ISO 178/A	5.0 %

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179/1eU	80 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	70 kJ/m²
Multi axis Instrumented Impact Energy		ISO 6603-2	4.80 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy		ISO 6603-2	13.0 J
Multi axis Instrumented Peak Impact Force		ISO 6603-2	650 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force		ISO 6603-2	1000 N

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC 60093	1E+15 ohms
Volume resistivity		IEC 60093	1E+13 ohms·cm
dielectric strength		IEC 60243-1	43 KV/mm
relative permittivity		IEC 60250	3.50
relative permittivity	relative permittivity		IEC 60250	3.20
Dissipation Factor		IEC 60250	6E-03
Dissipation Factor	Dissipation Factor		IEC 60250	0.015
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 0

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/C	60.0 °C
vicat		ISO 306/B50	200 °C
vicat	vicat		ISO 306/B120	200 °C
melting temperature		ISO 11357-3	214 °C
Linear coefficient of thermal expansion		ISO 11359-2	4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	1.5E-04 cm/cm/°C
Heat distortion temperature		ISO 75-2/B	205 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	175 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.