PA6 LANXESS GERMANY BKV215H2.0

Injection grade

US$ 3,310 / MT

FOB Guangzhou port, China

Electrical performance	Test Condition	Test Method	LANXESS GERMANY/BKV215H2.0
Dissipation factor	23°C,1MHz	IEC 60250	0.015
Volume resistivity	23°C	IEC 60093	1E+13 ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	43 KV/mm
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Surface resistivity		IEC 60093	1E+15 ohms
Relative permittivity	23°C,100Hz	IEC 60250	3.50
Dissipation factor	23°C,100Hz	IEC 60250	6E-03
Relative permittivity	23°C,1MHz	IEC 60250	3.20
thermal performance	Test Condition	Test Method	LANXESS GERMANY/BKV215H2.0
Vicat softening temperature	--	ISO 306/B50	200 °C
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1.5E-04 cm/cm/°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	60.0 °C
Hot deformation temperature		0.45MPa,Unannealed	ISO 75-2/B	205 °C
Vicat softening temperature	--	ISO 306/B120	200 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	175 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	4E-05 cm/cm/°C
Melting temperature		ISO 11357-3	214 °C
mechanical properties	Test Condition	Test Method	LANXESS GERMANY/BKV215H2.0
Tensile strain	Break,23°C	ISO 527-2/5	4.5 %
Bending strain	23°C	ISO 178/A	5.0 %
Bending modulus	23°C	ISO 178/A	4000 Mpa
tensile strength	Break,23°C	ISO 527-2/5	85.0 Mpa
bending strength	3.5%Strain,23°C	ISO 178/A	125 Mpa
Tensile modulus	23°C	ISO 527-2/1	4500 Mpa
bending strength	23°C4	ISO 178/A	130 Mpa
Physical properties	Test Condition	Test Method	LANXESS GERMANY/BKV215H2.0
Shrinkage rate	TD:120°C,4hr,2.00mm3	ISO 2577	0.15 %
Shrinkage rate		MD:280°C,2.00mm2	ISO 2577	0.59 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.0 %
Water absorption rate		Saturation,23°C	ISO 62	7.0 %
Shrinkage rate	TD:280°C,2.00mm2	ISO 2577	0.61 %
Apparent density		ISO 60	0.60 g/cm³
Shrinkage rate	MD:120°C,4hr,2.00mm3	ISO 2577	0.14 %
impact performance	Test Condition	Test Method	LANXESS GERMANY/BKV215H2.0
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	13.0 J
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	1000 N
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	70 kJ/m²
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	650 N
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80 kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	4.80 J
hardness	Test Condition	Test Method	LANXESS GERMANY/BKV215H2.0
Ball Pressure Test		ISO 2039-1	110 Mpa
flammability	Test Condition	Test Method	LANXESS GERMANY/BKV215H2.0
Extreme Oxygen Index		ISO 4589-2	22 %
UL flame retardant rating	3.2mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	650 °C
UL flame retardant rating	1.6mm	UL 94	HB
BurningBehavior		ISO 3795	passed
Supplementary Information	Test Condition	Test Method	LANXESS GERMANY/BKV215H2.0
ISO Shortcut		ISO 1874	PA6/66HI.GR.14-040.GF15