ABS HP-181 CNOOC&LG HUIZHOU
1322
- Unit Price:US$ 1,304 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:749.1MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High impact｜high flow｜High gloss｜Universal level
- Application Areas:Wear resistant accessories｜Electronic and Electrical Applications｜container｜chip
- Color:--
- Grade:Injection grade
Material Certification
TDS
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 6.4mm(Unannealed) 1.82MPa | ASTM D648 | 82 ℃ |
| Injection Molding Guide | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Pre drying temperature | 70~80 ℃ | ||
| Pre drying time | 3~4 hrs | ||
| Melting temperature | 200-240 ℃ | ||
| Mold temperature | 40~80 ℃ | ||
| Screw speed | 30~60 rpm | ||
| Back pressure | 10~30 kg/cm2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density | ASTM D792 | 1.04 g/cm³ | |
| Shrinkage rate | 3.2mm | ASTM D955 | 0.4~0.7 % |
| melt mass-flow rate | 220℃/10kg | ASTM D1238 | 40 g/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 3.2mm @Yield 50mm/min | ASTM D638 | 450 kg/cm2 |
| Elongation at Break | 3.2mm @Break 50mm/min | ASTM D638 | 18 % |
| bending strength | 6.4mm 10mm/min | ASTM D790 | 630 kg/cm2 |
| Bending modulus | 6.4mm 10mm/min | ASTM D790 | 24000 kg/cm2 |
| Izod Notched Impact Strength | 6.4mm(Notched) 23℃ | ASTM D256 | 26 kg.cm/cm |
| Rockwell hardness | R-Scale | ASTM D785 | 106 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.