Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS HP-181 CNOOC&LG HUIZHOU
--
Wear resistant accessories,Electronic and Electrical Applications,container,chip
High impact,high flow,High gloss,Universal level
MSDSMSDSTDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | CNOOC&LG HUIZHOU/HP-181 |
|---|---|---|---|
| Hot deformation temperature | 6.4mm(Unannealed) 1.82MPa | ASTM D648 | 82 ℃ |
| mechanical properties | Test Condition | Test Method | CNOOC&LG HUIZHOU/HP-181 |
|---|---|---|---|
| Bending modulus | 6.4mm 10mm/min | ASTM D790 | 24000 kg/cm2 |
| bending strength | 6.4mm 10mm/min | ASTM D790 | 630 kg/cm2 |
| Elongation at Break | 3.2mm @Break 50mm/min | ASTM D638 | 18 % |
| Izod Notched Impact Strength | 6.4mm(Notched) 23℃ | ASTM D256 | 26 kg.cm/cm |
| Rockwell hardness | R-Scale | ASTM D785 | 106 |
| tensile strength | 3.2mm @Yield 50mm/min | ASTM D638 | 450 kg/cm2 |
| Physical properties | Test Condition | Test Method | CNOOC&LG HUIZHOU/HP-181 |
|---|---|---|---|
| Density | ASTM D792 | 1.04 g/cm³ | |
| melt mass-flow rate | 220℃/10kg | ASTM D1238 | 40 g/10min |
| Shrinkage rate | 3.2mm | ASTM D955 | 0.4~0.7 % |
| Injection Molding Guide | Test Condition | Test Method | CNOOC&LG HUIZHOU/HP-181 |
|---|---|---|---|
| Back pressure | 10~30 kg/cm2 | ||
| Melting temperature | 200-240 ℃ | ||
| Mold temperature | 40~80 ℃ | ||
| Pre drying temperature | 70~80 ℃ | ||
| Pre drying time | 3~4 hrs | ||
| Screw speed | 30~60 rpm |