Material Description
- Material Properties:Antistatic｜ Glass fiber and inorganic filling｜Filler: Glass mineral｜65% filler by weight
- Application Areas:Electrical components｜parts｜Automotive Applications｜Fitness equipment
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | TORAY | 0.60 % | |
| coefficient of friction | ASTM D-1894 | 0.25 | |
| Taber wear resistance | ASTM D-1044 | 70 mg/1000次 | |
| Shrinkage rate | TORAY | 0.15 % | |
| 内部方法 | 0.60 % | ||
| 内部方法 | 0.30 % | ||
| Water absorption rate | ISO 62 | 0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 122 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 11443-A | 0.02 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| BarFlowLength | 内部方法 | 8.00 CM |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D-785 | 122 R | |
| elongation at break | ASTM D-638 | 1.6 % | |
| Impact strength of cantilever beam gap | ASTM D-256 | 80 J/m | |
| compressive strength | ASTM D-732 | 75 | |
| Flexural modulus | ASTM D-790 | 15.7 GPa | |
| Suspended wall beam without notch impact strength | ASTM D-256 | 15 KJ/m | |
| tensile strength | ASTM D-638 | 120 Mpa | |
| bending strength | ASTM D-790 | 145 Mpa | |
| tensile strength | ISO 527-2 | 110 Mpa | |
| Tensile strain | ISO 527-2 | 0.80 % | |
| Flexural modulus | ISO 178 | 19500 Mpa | |
| bending strength | ISO 178 | 195 Mpa | |
| shear strength | JISK7214 | 75.0 Mpa | |
| coefficient of friction | 0.25 | ||
| Taber abraser | ISO 9352 | 70.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 15 kJ/m² |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| TORAY | 60 | ||
| limiting pv value | TORAY | 815 KJ/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D-257 | 10 Ω.m | |
| IEC 60093 | 1E+08 ohms·cm | ||
| dielectric strength | IEC 60243-1 | 6.0 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 260 °C | |
| melting temperature | ISO 11357-3 | 278 °C | |
| Linear coefficient of thermal expansion | ASTM D-696 | 2.4 | |
| ASTM D-696 | 2.9 | ||
| Heat distortion temperature | ASTM D-648 | ＞260 °C | |
| melting temperature | DSC | 278 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 2E-05 cm/cm/°C | |
| ISO 11359-2 | 2.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.