Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A756M TORAY JAPAN
Torelina®
Electrical components,parts,Automotive Applications,Fitness equipment
Antistatic, Glass fiber and inorgani,Filler: Glass mineral,65% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/A756M |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 15 kJ/m² |
| Other performance | Test Condition | Test Method | TORAY JAPAN/A756M |
|---|---|---|---|
| limiting pv value | TORAY | 815 KJ/m | |
| 98MPa，流向 | TORAY | 60 |
| hardness | Test Condition | Test Method | TORAY JAPAN/A756M |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 122 |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/A756M |
|---|---|---|---|
| BarFlowLength | 320°C,1.00mm | 内部方法 | 8.00 CM |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/A756M |
|---|---|---|---|
| Water absorption rate | 23℃，24hr | ISO 11443-A | 0.02 % |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A756M |
|---|---|---|---|
| shear strength | 23°C | JISK7214 | 75.0 Mpa |
| Flexural modulus | 23℃ | ASTM D-790 | 15.7 GPa |
| coefficient of friction | 0.25 | ||
| tensile strength | ASTM D-638 | 120 Mpa | |
| Taber abraser | 1000Cycles | ISO 9352 | 70.0 mg |
| Suspended wall beam without notch impact strength | ASTM D-256 | 15 KJ/m | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 0.80 % |
| bending strength | 23°C | ISO 178 | 195 Mpa |
| Rockwell hardness | ASTM D-785 | 122 R | |
| elongation at break | 23℃ | ASTM D-638 | 1.6 % |
| compressive strength | ASTM D-732 | 75 | |
| bending strength | 23℃ | ASTM D-790 | 145 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 110 Mpa |
| Impact strength of cantilever beam gap | ASTM D-256 | 80 J/m | |
| Flexural modulus | 23°C | ISO 178 | 19500 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A756M |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 6.0 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+08 ohms·cm | |
| ASTM D-257 | 10 Ω.m |
| flammability | Test Condition | Test Method | TORAY JAPAN/A756M |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/A756M |
|---|---|---|---|
| coefficient of friction | ASTM D-1894 | 0.25 | |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.60 % |
| MD:3.00mm4 | 内部方法 | 0.30 % | |
| 流动 | TORAY | 0.15 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.020 % |
| Taber wear resistance | ASTM D-1044 | 70 mg/1000次 | |
| Shrinkage rate | 垂直 | TORAY | 0.60 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A756M |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 278 °C | |
| Heat distortion temperature | 1.82MPa，HDT | ASTM D-648 | ＞260 °C |
| Linear coefficient of thermal expansion | 流动 | ASTM D-696 | 2.4 |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2E-05 cm/cm/°C |
| melting temperature | DSC | 278 °C | |
| Linear coefficient of thermal expansion | 垂直 | ASTM D-696 | 2.9 |
| TD | ISO 11359-2 | 2.8E-05 cm/cm/°C |
Contact Us
Get App