Material Properties:Low friction coefficient｜Homopolymer｜wear resistant｜Lubricity｜Medium viscosity
Application Areas:Engine parts｜Household goods｜Engineering accessories｜Shell
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

other	Test Condition	Test Method	Test Result
notes			对金属和塑料具优异耐摩擦和磨耗

thermal performance	Test Method	Test Result
melt mass-flow rate	ASTM D1238	22 g/10min
Linear coefficient of thermal expansion	TMA法	10
UL flame retardant rating	UL 94	HB

Mechanical properties	Test Method	Test Result
Impact strength of cantilever beam gap	ASTM D256/ISO 179	59 kg·cm/cm(J/M)ft·lb/in
tensile strength	ASTM D638/ISO 527	60 kg/cm²(MPa)[Lb/in²]
elongation	ASTM D638/ISO 527	30 %
flexural modulus	ASTM D790/ISO 178	2740 kg/cm²(MPa)[Lb/in²]
bending strength	ASTM D790/ISO 178	90 kg/cm²(MPa)[Lb/in²]
tensile strength	ASTM D638	60 Mpa
Elongation at break	ASTM D638	30 %
bending strength	ASTM D790	90 Mpa
flexural modulus	ASTM D790	2740 Mpa
Impact strength of cantilever beam gap	ASTM D256	59 J/m

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.42
shrinkage rate		ASTM D955	1.8-2.2 %
melt mass-flow rate		ASTM D1238/ISO 1133	22 g/10min
Water absorption rate		ASTM D570/ISO 62	0.2 %
Water absorption rate	Water absorption rate		ASTM D570	0.2 %
shrinkage rate		旭化成法	1.8-2.2 %
shrinkage rate	shrinkage rate		旭化成法	1.8-2.2 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.