POM LM511 ASAHI JAPAN
TENAC™-C
Engine parts,Household goods,Engineering accessories,Shell
Low friction coefficient,Homopolymer,wear resistant,Lubricity,Medium viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/LM511 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 59 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 90 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2740 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790 | 90 Mpa | |
| elongation | ASTM D638/ISO 527 | 30 % | |
| Impact strength of cantilever beam gap | ASTM D256 | 59 J/m | |
| tensile strength | ASTM D638/ISO 527 | 60 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638 | 30 % | |
| Flexural modulus | ASTM D790 | 2740 Mpa | |
| tensile strength | ASTM D638 | 60 Mpa |
| other | Test Condition | Test Method | ASAHI JAPAN/LM511 |
|---|---|---|---|
| notes | 对金属和塑料具优异耐摩擦和磨耗 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/LM511 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.8-2.2 % | |
| density | ASTM D792/ISO 1183 | 1.42 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 22 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/LM511 |
|---|---|---|---|
| Shrinkage rate | 垂直方向 | 旭化成法 | 1.8-2.2 % |
| 平行方向 | 旭化成法 | 1.8-2.2 % | |
| Water absorption rate | ASTM D570 | 0.2 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/LM511 |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 22 g/10min | |
| Linear coefficient of thermal expansion | TMA法 | 10 | |
| UL flame retardant rating | UL 94 | HB |