PEI

PEI LNP™ STAT-KON™ EX99689C SABIC INNOVATIVE US

258

Unit Price:US$ 11,018 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜lubrication
Application Areas:Electrical and Electronic Applications｜Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	11.4 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	28 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.1 kJ/m²
Multi axis Instrumented Impact Energy		ISO 6603-2	2.41 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.35mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ASTM D790	242 Mpa
Bending modulus		ISO 178	7700 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	8000 Mpa
Tensile strain	Break	ISO 527-2	1.2 %
tensile strength	Break	ASTM D638	161 Mpa
Tensile modulus		ISO 527-2/1	12600 Mpa
Tensile modulus	Tensile modulus		ASTM D638	11700 Mpa
bending strength		ISO 178	216 Mpa
elongation	Break	ASTM D638	1.6 %
tensile strength	Break	ISO 527-2	137 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	3.3E-05 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	3.3E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	3.3E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	3.3E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	207 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	206 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.35 %
Water absorption rate	Water absorption rate	24hr,50%RH	ASTM D570	0.30 %
Shrinkage rate	MD:24hr	ISO 294-4	0.17 %
	Shrinkage rate	TD:24hr	ISO 294-4	0.36 %
		Shrinkage rate	TD：24hr	ASTM D955	0.40 %
		Shrinkage rate	Shrinkage rate	MD：24hr	ASTM D955	0.20 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	1.0E+2to1.0E+6 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI LNP™ STAT-KON™ EX99689C SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet