PEI EX99689C SABIC INNOVATIVE US
LNP™ STAT-KON™ 
Electrical and Electronic、Automotive components
Glass fiber reinforced、lubrication
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/EX99689C
Suspended wall beam without notch impact strength23°CISO 180/1U28 kJ/m²
Multi axis Instrumented Impact EnergyISO 6603-22.41 J
Impact strength of cantilever beam gap23°CISO 180/1A5.1 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D376311.4 J
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EX99689C
Tensile modulusISO 527-2/112600 Mpa
ASTM D63811700 Mpa
elongation断裂ASTM D6381.6 %
bending strengthISO 178216 Mpa
Tensile strain断裂ISO 527-21.2 %
Flexural modulusISO 1787700 Mpa
bending strengthASTM D790242 Mpa
tensile strength 断裂ASTM D638161 Mpa
断裂ISO 527-2137 Mpa
Flexural modulus50.0mm跨距ASTM D7908000 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/EX99689C
Surface ResistivityASTM D2571.0E+2to1.0E+6 ohms
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/EX99689C
UL flame retardant rating0.35mmUL 94V-0
physical property Test ConditionTest MethodSABIC INNOVATIVE US/EX99689C
Shrinkage rateMD:24小时ISO 294-40.17 %
MD：24小时ASTM D9550.20 %
Water absorption rate24hr,50%RHASTM D5700.30 %
平衡,23°C,50%RHISO 620.35 %
Shrinkage rateTD：24hrASTM D9550.40 %
TD:24小时ISO 294-40.36 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/EX99689C
Linear coefficient of thermal expansionTD：-40到40°CASTME8313.3E-05 cm/cm/°C
TD：-40到40°CISO 11359-23.3E-05 cm/cm/°C
MD：-40到40°CASTME8313.3E-05 cm/cm/°C
MD：-40到40°CISO 11359-23.3E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,64.0mm跨距，HDTISO 75-2/Af207 °C
1.8MPa,未退火,3.20mm，HDTASTM D648206 °C