MS TX-100S DENKA JAPAN
217
- Unit Price:US$ 2,039 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:70MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Weather resistance｜transparent
- Application Areas:Casters｜Optical level
- Color:--
- Grade:Injection grade
Technical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 具有与有机玻璃同样良好的透明性、耐气候性、表面强度、而且比有机玻璃树脂更有吸湿率比重小以及成型性好的聚合物 | ||
| purpose | 光学镜片.灯具罩.停车场棚架等有关外围设备 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Vicat softening temperature | ASTM D1525/ISO R306 | 100 ℃（℉） | |
| 50N荷重 | ISO 306 | 100 % | |
| Combustibility | UL 94 | HB | |
| Hot deformation temperature | 1.8MPa应力 | ISO 75-1 | 78 °C |
| Basic Performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 23℃ | ISO 1183 | 1.127 kg/cm3 |
| Total Light Transmittance | 2mmt | ISO 13468-1 | 92 % |
| turbidity | 2mmt | ISO 14762 | 0.2 % |
| Rockwell hardness | 23℃ | ISO 2039-2 | 86 (M) |
| mobility | 200℃，49N，Flow性 | ISO 1133 | 2.0 g/10分 |
| 200℃，98N，Flow性 | ISO 1133 | 26 g/10分 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 1.127 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Bending modulus | ASTM D790/ISO 178 | 3.320 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 111 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 86 | |
| bending strength | 2mm/min | ISO 178 | 111 Mpa |
| Tensile stress | 5mm/min，Break | ISO 527-1 | 73 Mpa |
| Charpy Notched Impact Strength | Notched,23℃ | ISO 179 | 2 kJ/m² |
| Bending modulus | 2mm/min | ISO 178 | 3.320 Mpa |
| Tensile strain | 5mm/min，Break | ISO 527-1 | 6 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.