Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MS TX-100S DENKA JAPAN
--
Casters、Optical level
Weather resistance、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DENKA JAPAN/TX-100S |
|---|---|---|---|
| mobility | 200℃，49N，流动性 | ISO 1133 | 2.0 g/10分 |
| density | 23℃ | ISO 1183 | 1.127 kg/cm3 |
| mobility | 200℃，98N，流动性 | ISO 1133 | 26 g/10分 |
| Total Light Transmittance | 2mmt | ISO 13468-1 | 92 % |
| Rockwell hardness | 23℃ | ISO 2039-2 | 86 (M) |
| Haze ratio | 2mmt | ISO 14762 | 0.2 % |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/TX-100S |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 111 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 3.320 kg/cm²(MPa)[Lb/in²] | |
| Tensile stress | 5mm/min，断裂 | ISO 527-1 | 73 Mpa |
| Charpy Notched Impact Strength | 缺口,23℃ | ISO 179 | 2 kJ/m² |
| Tensile strain | 5mm/min，断裂 | ISO 527-1 | 6 % |
| Rockwell hardness | ASTM D785 | 86 | |
| bending strength | 2mm/min | ISO 178 | 111 Mpa |
| Flexural modulus | 2mm/min | ISO 178 | 3.320 Mpa |
| other | Test Condition | Test Method | DENKA JAPAN/TX-100S |
|---|---|---|---|
| characteristic | 具有与有机玻璃同样良好的透明性、耐气候性、表面强度、而且比有机玻璃树脂更有吸湿率比重小以及成型性好的聚合物 | ||
| purpose | 光学镜片.灯具罩.停车场棚架等有关外围设备 |
| Physical properties | Test Condition | Test Method | DENKA JAPAN/TX-100S |
|---|---|---|---|
| density | 1.127 |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/TX-100S |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| vicat | 50N荷重 | ISO 306 | 100 % |
| ASTM D1525/ISO R306 | 100 ℃（℉） | ||
| combustibility | UL 94 | HB | |
| Heat distortion temperature | 1.8MPa应力 | ISO 75-1 | 78 °C |