PBT VALOX™ 420SEO-7001 SABIC INNOVATIVE JAPAN
327
- Unit Price:US$ 4,134 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜dimensional stability ｜High rigidity｜high strength｜heat-resisting
- Application Areas:Lawn equipment｜Garden equipment｜Industrial applications｜Automotive External Parts｜Electrical field｜Electronic field｜Architectural application field｜Outdoor applications｜Electrical appliances｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Automotive interior parts｜Casters｜Household goods｜Petroleum Applications｜Natural gas supplies｜sporting goods｜Textile application｜Lighting applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.610 cm³/g | |
| melt mass-flow rate | ASTM D1238 | 42 g/10 min | |
| Melt volume flow rate | ISO 1133 | 29.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.10 - 0.50 % | |
| 内部方法 | 0.50 - 0.70 % | ||
| 内部方法 | 0.40 - 0.80 % | ||
| 内部方法 | 0.50 - 1.0 % | ||
| Water absorption rate | ISO 62 | 0.090 % | |
| ISO 62 | 0.070 % | ||
| Outdoor applicability | UL 746C | f2 |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 119 | |
| ISO 2039-2 | 119 | ||
| ball-indentation hardness | ISO 2039-1 | 118 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-2 | |
| UL 94 | V-0 | ||
| UL 94 | 5VA | ||
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 32 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 12000 Mpa | |
| ISO 527-2/1 | 10000 Mpa | ||
| tensile strength | ASTM D638 | 120 Mpa | |
| ISO 527-2/5 | 120 Mpa | ||
| ASTM D638 | 120 Mpa | ||
| ISO 527-2/5 | 120 Mpa | ||
| elongation | ASTM D638 | 2.0 % | |
| ISO 527-2/5 | 1.9 % | ||
| ASTM D638 | 2.0 % | ||
| ISO 527-2/5 | 1.9 % | ||
| Flexural modulus | ASTM D790 | 9800 Mpa | |
| ISO 178 | 9500 Mpa | ||
| bending strength | ISO 178 | 180 Mpa | |
| ASTM D790 | 186 Mpa | ||
| Taber abraser | 内部方法 | 22.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 6.0 kJ/m² | |
| ISO 179/1eA | 7.0 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 50 kJ/m² | |
| ISO 179/1eU | 50 kJ/m² | ||
| Suspended wall beam without notch impact strength | ASTM D4812 | 620 J/m | |
| ISO 180/1U | 45 kJ/m² | ||
| ISO 180/1U | 45 kJ/m² | ||
| Dart impact | ASTM D3763 | 5.00 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Volume resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 24 KV/mm | |
| ASTM D149 | 19 KV/mm | ||
| IEC 60243-1 | 23 KV/mm | ||
| IEC 60243-1 | 22 KV/mm | ||
| IEC 60243-1 | 16 KV/mm | ||
| dielectric constant | ASTM D150 | 3.80 | |
| ASTM D150 | 3.70 | ||
| IEC 60250 | 3.30 | ||
| IEC 60250 | 3.30 | ||
| IEC 60250 | 3.30 | ||
| Dissipation Factor | ASTM D150 | 2.0E-3 | |
| ASTM D150 | 0.020 | ||
| IEC 60250 | 1.0E-3 | ||
| IEC 60250 | 1.0E-3 | ||
| IEC 60250 | 0.010 | ||
| arc resistance | ASTM D495 | PLC 6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| IEC 60112 | PLC 3 | ||
| IEC 60112 | PLC 4 | ||
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 80 % | ||
| Temperature at the rear of the barrel | 245 to 265 °C | ||
| Temperature in the middle of the barrel | 250 to 270 °C | ||
| Temperature at the front of the material cylinder | 255 to 275 °C | ||
| Spray nozzle temperature | 250 to 270 °C | ||
| Processing (melt) temperature | 255 to 275 °C | ||
| Temperature | 65 to 90 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 50 to 80 rpm | ||
| Exhaust hole depth | 0.025 to 0.038 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 212 °C | |
| ISO 75-2/Be | 220 °C | ||
| ASTM D648 | 200 °C | ||
| ISO 75-2/Ae | 195 °C | ||
| ISO 75-2/Af | 200 °C | ||
| vicat | ASTM D152510 | 200 °C | |
| ISO 306/A50 | 220 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | ASTM E831 | 2.5E-5 cm/cm/°C | |
| ISO 11359-2 | 2.5E-5 cm/cm/°C | ||
| ASTM E831 | 8.9E-5 cm/cm/°C | ||
| ISO 11359-2 | 8.9E-5 cm/cm/°C | ||
| ISO 11359-2 | 1.2E-4 cm/cm/°C | ||
| thermal conductivity | ISO 8302 | 0.25 W/m/K | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI | UL 746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.