Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PBT 420SEO-7001 SABIC INNOVATIVE JAPAN

VALOX™

Lawn equipment,Garden equipment,Industrial applications,Automotive External Parts,Electrical field,Electronic field,Architectural application field,Outdoor applications,Electrical appliances,Engine hood parts,Medical supplies,Nursing supplies,Plastic bag,Automotive interior parts,Casters,Household goods,Petroleum Applications,Natural gas supplies,sporting goods,Textile application,Lighting applications

Glass fiber reinforced,dimensional stability ,High rigidity,high strength,heat-resisting

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/420SEO-7001
Ball Pressure Test	H 358/30	ISO 2039-1	118 Mpa
Rockwell hardness	R -Sale	ISO 2039-2	119
Rockwell hardness		R-Scale	ASTM D785	119

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/420SEO-7001
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	212 °C
		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	200 °C
		0.45 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Be	220 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	200 °C
		1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Ae	195 °C
Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	8.9E-5 cm/cm/°C
		Across Flow : 23 to 80°C	ISO 11359-2	1.2E-4 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	2.5E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	8.9E-5 cm/cm/°C
		Flow : 23 to 80°C	ISO 11359-2	2.5E-5 cm/cm/°C
RTI		UL 746	140 °C
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
thermal conductivity		ISO 8302	0.25 W/m/K
Vicat softening temperature	--	ASTM D152510	200 °C
Vicat softening temperature		--	ISO 306/A50	220 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/420SEO-7001
Bending modulus	--6	ISO 178	9500 Mpa
Bending modulus		50.0 mm Span5	ASTM D790	9800 Mpa
bending strength	Break, 50.0 mm Span5	ASTM D790	186 Mpa
bending strength		--	ISO 178	180 Mpa
elongation	Break	ISO 527-2/5	1.9 %
		Yield4	ASTM D638	2.0 %
		Break4	ASTM D638	2.0 %
		Yield	ISO 527-2/5	1.9 %
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	22.0 mg
Tensile modulus	--3	ASTM D638	12000 Mpa
Tensile modulus		--	ISO 527-2/1	10000 Mpa
tensile strength	Break	ISO 527-2/5	120 Mpa
		Break4	ASTM D638	120 Mpa
		Yield	ISO 527-2/5	120 Mpa
		Yield4	ASTM D638	120 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/420SEO-7001
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index	Solution B	IEC 60112	PLC 4
			UL 746	PLC 3
		--	IEC 60112	PLC 3
Dielectric constant	50 Hz	IEC 60250	3.30
		1 MHz	IEC 60250	3.30
		1 MHz	ASTM D150	3.70
		100 Hz	ASTM D150	3.80
		60 Hz	IEC 60250	3.30
Dielectric strength	3.20 mm, in Oil	IEC 60243-1	16 KV/mm
		1.60 mm, in Oil	ASTM D149	24 KV/mm
		3.20 mm, in Air	ASTM D149	19 KV/mm
		0.800 mm, in Oil	IEC 60243-1	23 KV/mm
		1.60 mm, in Oil	IEC 60243-1	22 KV/mm
Dissipation factor	1 MHz	ASTM D150	0.020
		50 Hz	IEC 60250	1.0E-3
		60 Hz	IEC 60250	1.0E-3
		100 Hz	ASTM D150	2.0E-3
		1 MHz	IEC 60250	0.010
High arc combustion index		UL 746	PLC 0
High voltage arc tracing rate		UL 746	PLC 4
Hot wire ignition		UL 746	PLC 2
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Volume resistivity		ASTM D257	> 1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/420SEO-7001
melt mass-flow rate	250°C/5.0 kg	ASTM D1238	42 g/10 min
Melt Volume Flow Rate (MVR)	250°C/5.0 kg	ISO 1133	29.0 cm3/10min
Outdoor applicability		UL 746C	f2
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 1.0 %
		Flow : 3.20 mm	Internal Method	0.50 - 0.70 %
		Flow 2	Internal Method	0.10 - 0.50 %
		Across FlowFlow 2	Internal Method	0.40 - 0.80 %
Specific volume		ASTM D792	0.610 cm³/g
Water absorption rate	Saturation, 23°C	ISO 62	0.090 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.070 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/420SEO-7001
Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.0 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	6.0 kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	5.00 J
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	50 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	50 kJ/m²
Suspended wall beam without notch impact strength	-30°C8	ISO 180/1U	45 kJ/m²
		23°C	ASTM D4812	620 J/m
		23°C8	ISO 180/1U	45 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/420SEO-7001
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	32 %
UL flame retardant rating	0.71 mm	UL 94	V-0
		0.40 mm	UL 94	V-2
		2.0 mm	UL 94	5VA

injection	Test Condition	Test Method	SABIC INNOVATIVE JAPAN/420SEO-7001
Back pressure			0.300 to 0.700 Mpa
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Exhaust hole depth			0.025 to 0.038 mm
Mold temperature			65 to 90 °C
Processing (melt) temperature			255 to 275 °C
Screw speed			50 to 80 rpm
Spray nozzle temperature			250 to 270 °C
Suggested injection volume			40 to 80 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			255 to 275 °C
Temperature at the rear of the barrel			245 to 265 °C
Temperature in the middle of the barrel			250 to 270 °C

Get App