PC PANLITE® LV-2225Z TEIJIN SINGAPORE

185

Unit Price:US$ 3,342 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Low viscosity｜transparent｜UV resistance
Application Areas:Electrical field｜Electronic field｜currency
Color:--
Grade:High liquidity level

Material Certification

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Melt volume flow rate		ISO 1133	15.0 cm3/10min
Shrinkage rate		内部方法	0.50-0.70 %
Shrinkage rate	Shrinkage rate		内部方法	0.50-0.70 %
Water absorption rate		ISO 62	0.20 %

optical performance	Test Method	Test Result
refractive index	ASTM D542	1.585
transmissivity	ASTM D1003	88.0 %
transmittance	ASTM D1003/ISO 13468	88 %
refractive index	ASTM D542/ISO 489	1.585

other	Test Condition	Test Method	Test Result
characteristic			低粘度抗紫外线性能良好
purpose			电子电器领域应用透明或半透明配件电器用具

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-2
	UL flame retardant rating		UL 94	V-2
	UL flame retardant rating	UL flame retardant rating		UL 94	V-2
Burning wire flammability index		IEC 60695-2-12	850 °C
Burning wire flammability index	Burning wire flammability index		IEC 60695-2-12	960 °C
Hot filament ignition temperature		IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature		IEC 60695-2-13	875 °C

Mechanical properties	Test Method	Test Result
Nominal tensile fracture strain	ISO 527-2/50	>50 %
Flexural modulus	ISO 178	2400 Mpa
bending strength	ISO 178	94.0 Mpa
Tensile modulus	ISO 527-2/1	2400 Mpa
tensile strength	ISO 527-2/50	61.0 Mpa
Tensile strain	ISO 527-2/50	6.0 %
elongation at break	ASTM D638/ISO 527	50 %
Tensile modulus	ASTM D638/ISO 527	2130 kg/cm²(MPa)[Lb/in²]
Rockwell hardness	ASTM D785	M 77
Flexural modulus	ASTM D790/ISO 178	2260 kg/cm²(MPa)[Lb/in²]
bending strength	ASTM D790/ISO 178	94 kg/cm²(MPa)[Lb/in²]

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	NoBreak

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
dielectric strength		IEC 60243-1	30 KV/mm
dielectric constant		IEC 60250	3.10
dielectric constant	dielectric constant		IEC 60250	3.00
Dissipation Factor		IEC 60250	1E-03
Dissipation Factor	Dissipation Factor		IEC 60250	9E-03
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 3

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.2

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/B	141 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	125 °C
vicat		ISO 306/B50	146 °C
Linear coefficient of thermal expansion		ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	7E-05 cm/cm/°C
RTI Elec		UL 746	125 °C
RTI Imp		UL 746	115 °C
RTI Str		UL 746	125 °C
Combustibility (rate)		UL 94	V-2
vicat		ASTM D1525/ISO R306	148 ℃（℉）

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App