Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LV-2225Z TEIJIN SINGAPORE
PANLITE®
Electrical field、Electronic field、currency
Low viscosity、transparent、UV resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN SINGAPORE/LV-2225Z |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | TEIJIN SINGAPORE/LV-2225Z |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 94 kg/cm²(MPa)[Lb/in²] | |
| Tensile stress | 屈服 | ISO527-2/50 | 61.0 Mpa |
| Tensile modulus | ISO527-2/1 | 2400 Mpa | |
| Flexural modulus | ASTM D790/ISO 178 | 2260 kg/cm²(MPa)[Lb/in²] | |
| Bending modulus 2 | ISO178 | 2400 Mpa | |
| Bending stress 2 | ISO178 | 94.0 Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 2130 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 屈服 | ISO527-2/50 | 6.0 % |
| elongation at break | ASTM D638/ISO 527 | 50 % | |
| Rockwell hardness | ASTM D785 | M 77 | |
| Nominal tensile fracture strain | ISO527-2/50 | >50 % |
| Electrical performance | Test Condition | Test Method | TEIJIN SINGAPORE/LV-2225Z |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Dielectric strength 3 | IEC60243-1 | 30 KV/mm | |
| CTI | IEC60112 | 225 V | |
| dielectric constant | 1MHz | IEC60250 | 3.00 |
| Dissipation Factor | 100Hz | IEC60250 | 1E-03 |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| dielectric constant | 100Hz | IEC60250 | 3.10 |
| Dissipation Factor | 1MHz | IEC60250 | 9E-03 |
| optical performance | Test Condition | Test Method | TEIJIN SINGAPORE/LV-2225Z |
|---|---|---|---|
| refractive index | ASTMD542 | 1.585 | |
| transmissivity | 3000µm | ASTMD1003 | 88.0 % |
| refractive index | ASTM D542/ISO 489 | 1.585 | |
| transmittance | ASTM D1003/ISO 13468 | 88 % |
| other | Test Condition | Test Method | TEIJIN SINGAPORE/LV-2225Z |
|---|---|---|---|
| 低粘度 抗紫外线性能良好 | |||
| purpose | 电子电器领域应用 透明或半透明配件 电器用具 |
| Physical properties | Test Condition | Test Method | TEIJIN SINGAPORE/LV-2225Z |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.2 |
| flammability | Test Condition | Test Method | TEIJIN SINGAPORE/LV-2225Z |
|---|---|---|---|
| Hot filament ignition temperature | 3.0mm | IEC60695-2-13 | 875 °C |
| UL flame retardant rating | 3.0mm | UL94 | V-2 |
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 850 °C |
| UL flame retardant rating | 1.5mm | UL94 | V-2 |
| Hot filament ignition temperature | 1.5mm | IEC60695-2-13 | 850 °C |
| UL flame retardant rating | 0.40mm | UL94 | V-2 |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | TEIJIN SINGAPORE/LV-2225Z |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 15.0 cm3/10min |
| Water absorption rate | 23°C,24hr | ISO62 | 0.20 % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.50to0.70 % |
| TD:4.00mm | 内部方法 | 0.50to0.70 % |
| Thermal performance | Test Condition | Test Method | TEIJIN SINGAPORE/LV-2225Z |
|---|---|---|---|
| TD | ISO11359-2 | 7E-05 cm/cm/°C | |
| 0.45MPa,未退火 | ISO75-2/B | 141 °C | |
| vicat | ISO306/B50 | 146 °C | |
| RTI Elec | 1.5mm | UL746 | 125 °C |
| vicat | ASTM D1525/ISO R306 | 148 ℃（℉） | |
| RTI Str | 1.5mm | UL746 | 125 °C |
| 1.8MPa,未退火 | ISO75-2/A | 125 °C | |
| RTI Imp | 1.5mm | UL746 | 115 °C |
| MD | ISO11359-2 | 7E-05 cm/cm/°C | |
| Combustibility (rate) | UL94 | V-2 |