Material Description

Material Properties:Glass fiber reinforced｜Filler: Glass fiber reinforced material｜30%｜Filler by weight
Application Areas:Household appliances｜Automotive sector｜Aerospace｜Electronic field｜Electrical field｜Aerospace Applications｜Communication equipment｜Application in the automotive field
Color:--
Grade:Injection grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			30%玻纤增强

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	35 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	0.38mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256/ISO 179	25 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	20 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	2.7 %
Tensile modulus		ASTM D638/ISO 527	13500 kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	165 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	- kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	195 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ISO 527-2/1A/1	13000 Mpa
tensile strength	Break	ISO 527-2/1A/5	130 Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.8 %
Bending modulus	23°C	ISO 178	12000 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	HDT	ASTM D648/ISO 75	- ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	268 ℃（℉）
Melting temperature			335 ℃（℉）
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	265 °C
Melting temperature		ISO 11357-3	335 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3E-06 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1680
Water absorption rate		ASTM D570/ISO 62	0.002 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257/IEC 60093	1.00E+16 Ω
Volume resistivity		ASTM D257/IEC 60093	1.00E+17 Ω.cm
Surface resistivity		IEC 60093	>1.0E+16 ohms
Volume resistivity		IEC 60093	>1.0E+16 ohms·cm
Dielectric strength		IEC 60243-1	36 KV/mm
Relative permittivity	1MHz	IEC 60250	4.00
Relative permittivity	Relative permittivity	2.05GHz	Internal Method	4.16
Dissipation factor	1MHz	IEC 60250	0.031
Dissipation factor	Dissipation factor	2.05GHz	Internal Method	5E-03
Compared to the anti leakage trace index		IEC 60112	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

LCP ZENITE® 6130L-WT010 DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet