LCP 6130L-WT010 DUPONT USA
ZENITE®
Household appliances、Automotive sector、Aerospace、Electronic field、Electrical field、Aerospace Applications、Communication equipment、Application in the automo
Glass fiber reinforced、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/6130L-WT010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 35 kJ/m² |
| Electrical performance | Test Condition | Test Method | DUPONT USA/6130L-WT010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Surface Resistivity | ASTM D257/IEC 60093 | 1.00E+16 Ω | |
| relative permittivity | 2.05GHz | 内部方法 | 4.16 |
| dielectric strength | IEC 60243-1 | 36 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
| Dissipation Factor | 2.05GHz | 内部方法 | 5E-03 |
| relative permittivity | 1MHz | IEC 60250 | 4.00 |
| Volume resistivity | ASTM D257/IEC 60093 | 1.00E+17 Ω.cm | |
| Surface Resistivity | IEC 60093 | >1.0E+16 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.031 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/6130L-WT010 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 20 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 195 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | - kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2/1A/1 | 13000 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 12000 Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 13500 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 130 Mpa |
| elongation at break | ASTM D638/ISO 527 | 2.7 % | |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.8 % |
| tensile strength | ASTM D638/ISO 527 | 165 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | DUPONT USA/6130L-WT010 |
|---|---|---|---|
| characteristic | 30%玻纤增强 |
| Physical properties | Test Condition | Test Method | DUPONT USA/6130L-WT010 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1680 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.002 % |
| flammability | Test Condition | Test Method | DUPONT USA/6130L-WT010 |
|---|---|---|---|
| UL flame retardant rating | 0.38mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 |
| Thermal performance | Test Condition | Test Method | DUPONT USA/6130L-WT010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 335 °C | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 268 ℃（℉） |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 265 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3E-06 cm/cm/°C |
| melting temperature | 335 ℃（℉） | ||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 7E-05 cm/cm/°C |