TPE Hytrel®  5526 DUPONT USA

225
  • Unit Price:US$ 3,786 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    20MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Weather resistance｜UV resistance｜High mobility｜Thermal stability
  • Application Areas:Automotive sector｜Electrical appliances｜Fitness equipment｜Electronic field｜Electrical field
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of cantilever beam gap23°CISO 8256/1270 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Charpy Notched Impact Strength-40°CISO 179/1eA30 kJ/m²
Charpy Notched Impact Strength-30°C,Partial BreakISO 179/1eA150 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eANoBreak
flammabilityTest ConditionTest MethodTest Result
Extreme Oxygen IndexISO 4589-221 %
UL flame retardant rating3.0mmIEC 60695-11-10,-20HB
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
FMVSS flammabilityFMVSS302SE/B
Fogging-G-valuecondensateISO 64521E-04 g
UL flame retardant rating3.0mmUL 94HB
UL flame retardant rating1.5mmUL 94HB
Burning rate1.00mmISO 379528 mm/min
elastomerTest ConditionTest MethodTest Result
tear strength横向FlowISO 34-1130 kN/m
tear strengthFlowISO 34-1130 kN/m
mechanical propertiesTest ConditionTest MethodTest Result
Nominal tensile fracture strainISO 527-2780 %
Tensile strainBreakISO 527-2>300 %
Tensile strainYieldISO 527-235 %
tensile strength50%StrainISO 527-214.0 Mpa
tensile strength10%StrainISO 527-211.0 Mpa
tensile strength5.0%StrainISO 527-26.90 Mpa
tensile strengthBreakISO 527-240.0 Mpa
tensile strengthYieldISO 527-215.0 Mpa
Tensile modulusISO 527-2190 Mpa
Tensile creep modulus1hrISO 899-1170 Mpa
Tensile creep modulus1000hrISO 899-1130 Mpa
Bending modulusISO 178200 Mpa
Wear resistanceISO 4649120 mm³
thermal performanceTest ConditionTest MethodTest Result
Vicat softening temperature--ISO 306/A50180 °C
Glass transition temperatureISO 11357-2-20.0 °C
Brittle temperatureISO 974-98.0 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A45.0 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B65.0 °C
Vicat softening temperature--ISO 306/B5075.0 °C
Melting temperatureISO 11357-3203 °C
Linear coefficient of thermal expansionMD：--ISO 11359-22E-04 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to23°CISO 11359-21.8E-04 cm/cm/°C
Linear coefficient of thermal expansionTD：--ISO 11359-22E-04 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to23°CISO 11359-21.7E-04 cm/cm/°C
Linear coefficient of thermal expansionTD：EffectiveThermalDiffusivityISO 11359-29E-08 m²/s
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateMDISO 294-41.4 %
Water absorption rate23°C,24hrISO 620.60 %
Shrinkage rateTDISO 294-41.4 %
Melt Volume Flow Rate (MVR)220°C/2.16kgISO 113317.5 cm3/10min
melt mass-flow rateISO 113318 g/10min
densityISO 11831.19 g/cm³
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.20 %
Water absorption rateSaturation,23°C,2.00mmISO 620.60 %
MediumDensity1.04 g/cm³
SpecificHeatCapacity of Melt2110 J/kg/°C
ThermalConductivityofMelt0.19 W/m/K
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityIEC 600934E+13 ohms·cm
Dielectric strengthIEC 60243-120 KV/mm
Compared to the anti leakage trace indexIEC 60112 V
Dissipation factor1MHzIEC 602500.038
Dissipation factor100HzIEC 602509E-03
Relative permittivity1MHzIEC 602504.60
Relative permittivity100HzIEC 602504.90
hardnessTest ConditionTest MethodTest Result
Shore hardnessShoreD,15SecISO 86851
Shore hardnessShoreDISO 86855
Supplementary InformationTest ConditionTest MethodTest Result
OdorVDA2705.00
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.