Material Description
- Material Properties:High toughness｜Heat sealing performance｜high strength
- Application Areas:film
- Color:--
- Grade:Blow molding grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTMD1238 | 1.5 g/10min | |
| Content of comonomer | 内部方法 | 9.7 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D2457 | 65 | |
| Haze ratio | ASTM D1003 | 5.8 % | |
| ISO 14782 | 5.8 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D-1238 | 1.5 g/10min | |
| ISO 1133 | 1.5 g/10min | ||
| Monomer content | Internal Method | % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ASTM D-882 | 400 % | |
| ISO 527-3 | 400 % | ||
| ISO 527-3 | 470 % | ||
| Dart impact | ASTM D-1709B | 580 g | |
| ISO 7765-1/B | 580 g | ||
| Elmendorf tear strength | ASTM D-1922 | 510 g | |
| ASTM D-1922 | 380 g | ||
| ISO 6383-2 | 1700 N | ||
| ISO 6383-2 | 2300 N | ||
| tensile strength | ASTM D-638 | 8.39 MPa | |
| ISO 527-2/508 | 8.39 MPa | ||
| ASTM D-638 | 22.5 MPa | ||
| ISO 527-2/508 | 22.5 MPa | ||
| ASTM D-882 | 11.8 MPa | ||
| ASTM D-882 | 10.9 MPa | ||
| ISO 527-3 | 10.9 MPa | ||
| ISO 527-3 | 11.8 MPa | ||
| ASTM D-882 | 38.1 MPa | ||
| ASTM D-882 | 37.9 MPa | ||
| ISO 527-3 | 37.9 MPa | ||
| ISO 527-3 | 38.1 MPa | ||
| elongation at break | ASTM D-882 | 470 % | |
| tensile strength | ASTM D638 | 8.39 Mpa | |
| ISO 527-2/508 | 8.39 Mpa | ||
| ASTM D638 | 22.5 Mpa | ||
| ISO 527-2/508 | 22.5 Mpa | ||
| elongation | ASTM D638 | 640 % | |
| ISO 527-2/508 | 640 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D882 | 10.9 Mpa | |
| ISO 527-3 | 11.8 Mpa | ||
| ISO 527-3 | 10.9 Mpa | ||
| ASTMD882 | 37.9 Mpa | ||
| ASTMD882 | 38.1 Mpa | ||
| elongation | ASTMD882 | 400 % | |
| ASTMD882 | 470 % | ||
| Dart impact | ASTMD1709B | 580 g | |
| Elmendorf tear strength | ASTM D1922 | 380 g | |
| ASTM D1922 | 510 g | ||
| ISO 6383-2 | 1700 N | ||
| ISO 6383-2 | 2300 N | ||
| tensile strength | ASTM D882 | 11.8 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D-1525 | 81.1 ℃ | |
| ISO 306 | 81.1 ℃ | ||
| melting temperature | Internal Method | 97.8 ℃ | |
| vicat | ASTMD1525 | 81.1 °C | |
| melting temperature | 内部方法 | 97.8 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.