thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火	ISO 75-2/Bf	215 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火	ISO 75-2/Af	195 °C

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	65 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
viscosity number	H2SO4（硫酸）	ISO 307	125 cm³/g

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
drying time			3.0 to 6.0 hr
Suggested maximum moisture content			0.040 to 0.10 %
Suggested maximum material return ratio			20 %
Processing (melt) temperature			240 to 280 °C
mold temperature			50 to 90 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A/1	10500 Mpa
tensile strength	断裂	ISO 527-2/1A/5	175 Mpa
Tensile strain	断裂	ISO 527-2/1A/5	3.2 %
flexural modulus		ISO 178	10000 Mpa
bending strength	3.7% 应变	ISO 178	280 Mpa
bending strength	bending strength	3.5% 应变	ISO 178	280 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.